STACKING FAULT ENERGY OF SOME COPPER SILICON ALLOYS

被引:38
作者
NORDSTROM, TV
BARRETT, CR
机构
[1] Department of Materials Science, Stanford University
来源
ACTA METALLURGICA | 1969年 / 17卷 / 02期
关键词
D O I
10.1016/0001-6160(69)90134-5
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The composition and temperature dependence of the stacking fault energy in a series of dilute Cu-Si alloys was measured using extended node techniques, texture measurements, and X-ray fault probability measurements. The node and fault probability measurements indicate a smooth decrease in stacking fault energy with silicon content between 0 and 6.9 at. % silicon. Texture measurements indicate a maximum in the stacking fault energy-composition curve at low silicon contents but this is probably due to some factor other than a true increase in fault energy. Using node measurements the stacking fault energy in the Cu-6.9% Si alloy was observed to irreversibly increase slightly when heating to temperatures above 300°C. © 1969.
引用
收藏
页码:139 / +
页数:1
相关论文
共 26 条
[1]   STACKING FAULT ENERGY IN SILICON [J].
AERTS, E ;
SIEMS, R ;
DELAVIGNETTE, P ;
AMELINCKX, S .
JOURNAL OF APPLIED PHYSICS, 1962, 33 (10) :3078-&
[2]   ELECTRON OPTICAL STUDY OF BASAL DISLOCATIONS IN GRAPHITE [J].
AMELINCKX, S ;
DELAVIGNETTE, P .
JOURNAL OF APPLIED PHYSICS, 1960, 31 (12) :2126-2135
[3]   SHAPE OF 3-FOLD EXTENDED NODES [J].
BROWN, LM ;
THOLEN, AR .
DISCUSSIONS OF THE FARADAY SOCIETY, 1964, (38) :35-+
[4]  
CHRISTIAN JW, 1965, ALLOYING BEHAVIOR EF, P105
[5]  
DILLAMORE IL, 1965, PHILOS MAG, V11, P517
[6]   SUBSTITUTIONAL SOLUTION HARDENING [J].
FLEISCHER, RL .
ACTA METALLURGICA, 1963, 11 (03) :203-&
[7]   FORMATION OF EXTRINSIC-INTRINSIC FAULTING [J].
GALLAGHER, PC ;
WASHBURN, J .
PHILOSOPHICAL MAGAZINE, 1967, 15 (137) :969-+
[8]  
GALLAGHER PC, 1968, T METALL SOC AIME, V242, P103
[9]   STACKING-FAULT ENERGY IN AG-IN SERIES [J].
GALLAGHER, PC ;
WASHBURN, J .
PHILOSOPHICAL MAGAZINE, 1966, 14 (131) :971-+
[10]  
GALLAGHER PCJ, 1967, FAL M AIME CLEV