INVESTIGATION OF TITANIUM-MOLYBDENUM BINARY PHASE-DIAGRAM

被引：15

作者：

TERAUCHI, S

MATSUMOTO, H

SUGIMOTO, T

KAMEI, K

机构：

[1] OSAKA YAKIN HEAT TREATING CO LTD, OSAKA, JAPAN

[2] OSAKA IND UNIV, FAC ENGN, OSAKA, JAPAN

[3] KANSAI UNIV, FAC ENGN, SUITA, JAPAN

来源：

JOURNAL OF THE JAPAN INSTITUTE OF METALS | 1977年 / 41卷 / 06期

关键词：

TITANIUM MOLYBDENUM ALLOYS - Testing;

D O I：

10.2320/jinstmet1952.41.6_632

中图分类号：

学科分类号：

摘要：

The Ti-Mo phase diagram was investigated by optical microscopic observation, electrical resistance measurement X-ray diffraction and transmission electron micrographic observation. The miscibility gap was found to exist in the region above 675 degree C where no gap has been reported previously. The maximum temperature of this miscibility gap is 795 degree C for Ti-32. 5 wt% Mo alloy. The beta reversible reaction ( alpha plus beta //2) monotectoid reaction is found at 675 degree C and the monotectoid point lies at the composition range from Ti-20 to 22. 5 wt% Mo.

引用

页码：632 / 637

页数：6

共 15 条

[1]

BLACKBURN MJ, 1968, T METALL SOC AIME, V242, P2461

[2] IDENTIFICATION OF AN IMPURITY PHASE IN METASTABLE BETA-TITANIUM ALLOYS [J].

BOWEN, AW ;

STUBBINGTON, CA .

JOURNAL OF THE LESS-COMMON METALS, 1970, 20 (04) :367-+

[3]

CRAIGHEAD CM, 1950, T AM I MIN MET ENG, V188, P485

[4] ATOMIC ARRANGEMENTS IN TITANIUM-MOLYBDENUM SOLID SOLUTIONS [J].

DUPOUY, JM ;

AVERBACH, BL .

ACTA METALLURGICA, 1961, 9 (08) :755-763

[5]

DUWEZ P, 1951, T AM I MIN MET ENG, V191, P765

[6]

DUWEZ P, 1952, T AIME, V194, P518

[7]

GRUMGRZHIMAILO NV, 1957, ZH NEORG KHIM+, V2, P2426

[8]

HANSEN M, 1951, T AM I MIN MET ENG, V191, P881

[9]

Harmon E.L., 1961, T ASM, V53, P43

[10]

KAUFMAN L, 1973, TITANIUM SCI TECHNOL, V2, P773

← 1 2 →