FIBER-REINFORCED CEMENT-BASED COMPOSITES UNDER TENSILE IMPACT

被引：50

作者：

BANTHIA, N ^{[1
]}

CHOKRI, K ^{[1
]}

OHAMA, Y ^{[1
]}

MINDESS, S ^{[1
]}

机构：

[1] NIHON UNIV,COLL ENGN,KORIYAMA,FUKUSHIMA 963,JAPAN

来源：

ADVANCED CEMENT BASED MATERIALS | 1994年 / 1卷 / 03期

关键词：

CEMENT COMPOSITES; IMPACT; MICRO-FIBERS; STRENGTH; TENSION; TOUGHNESS;

D O I：

10.1016/1065-7355(94)90044-2

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

In many civil engineering structures, adequate resistance of the material to suddenly applied loads is essential. This article describes the improvements in the impact resistance of cement matrices when reinforced with high volume fractions of carbon, steel, and polypropylene micro-fibers. Tensile briquettes were fractured under a rapidly applied load using a newly designed instrumented impact machine. Strength and fracture energy values were measured. When compared with static test results, considerable sensitivity to stress rate was noted. The composites were found to be stronger and tougher under impact and the improvements were more pronounced at higher fiber volume fractions.

引用

页码：131 / 141

页数：11

共 40 条

[1] IMPACT TESTING OF CONCRETE USING A DROP-WEIGHT IMPACT MACHINE
BANTHIA, N
MINDESS, S
BENTUR, A
PIGEON, M
[J]. EXPERIMENTAL MECHANICS, 1989, 29 (01) : 63 - 69
[2] Banthia N, 1992, CEMENT CONCRETE COMP, V14, P119
[3] BANTHIA N, 1990, MATERIALS RES SOC S, V211, P25
[4] Banthia N., 1987, MATER STRUCT, V20, P293
[5] BANTHIA N, 1994, IN PRESS ASCE J MATE
[6] Banthia N., 1989, P INT C FIB REINF CE, P251
[7] Banthia N.P., 1987, THESIS U BRIT COLUMB
[8] DYNAMIC STRENGTH OF POLYMER MODIFIED AND FIBER-REINFORCED CONCRETES
BHARGAVA, J
REHNSTROM, A
[J]. CEMENT AND CONCRETE RESEARCH, 1977, 7 (02) : 199 - 208
[9] BIRKIMER DL, 1971, 12TH P S ROCK MECH, P573
[10] EVANS RH, 1942, J I CIVIL ENG, V18, P296

← 1 2 3 4 →