CRYSTALLIZATION BY BALL-MILLING - A WAY TO PRODUCE SOFT-MAGNETIC MATERIALS IN POWDERED FORM

被引：4

作者：

GIRI, AK ^{[1
]}

GONZALEZ, JM ^{[1
]}

GONZALEZ, J ^{[1
]}

机构：

[1] UNIV BASQUE COUNTRY, FAC QUIM, DEPT FIS MAT, E-20080 SAN SEBASTIAN, SPAIN

来源：

IEEE TRANSACTIONS ON MAGNETICS | 1995年 / 31卷 / 06期

关键词：

D O I：

10.1109/20.489811

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

We have produced by high energy ball milling a nanocrystalline material in powdered form. The starting material was amorphous melt spun Fe64.5Co18Si1B16C0.5. From the results of a systematic study of the dependence of the saturation coercive force on the annealing time and temperature it was evidenced the possibility of achieving coercivities as low as 0.150 +/- 0.004 Oe and therefore comparable with those measured in the as-quenched highly magnetostrictive melt spun samples of similar composition.

引用

页码：3904 / 3906

页数：3

共 4 条

[1] NANOCRYSTALLINE SOFT MAGNETIC-MATERIALS [J].

HERZER, G .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1992, 112 (1-3) :258-262

[2] GRAIN-SIZE DEPENDENCE OF COERCIVITY AND PERMEABILITY IN NANOCRYSTALLINE FERROMAGNETS [J].

HERZER, G .

IEEE TRANSACTIONS ON MAGNETICS, 1990, 26 (05) :1397-1402

[3] GRAIN-STRUCTURE AND MAGNETISM OF NANOCRYSTALLINE FERROMAGNETS [J].

HERZER, G .

IEEE TRANSACTIONS ON MAGNETICS, 1989, 25 (05) :3327-3329

[4] DEFORMATION-INDUCED CRYSTALLIZATION DUE TO INSTABILITY IN AMORPHOUS FEZR ALLOYS [J].

TRUDEAU, ML .

APPLIED PHYSICS LETTERS, 1994, 64 (26) :3661-3663

← 1 →