A GENERAL APPROACH TO CREEP FAILURE RESULTING FROM WEDGE CRACK GROWTH

被引：17

作者：

WILLIAMS, JA

机构：

[1] Materials Division, Central Electricity Research Laboratories, Leatherhead, Surrey, Kelvin Avenue

来源：

PHILOSOPHICAL MAGAZINE | 1969年 / 20卷 / 165期

关键词：

D O I：

10.1080/14786436908228734

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A model is suggested to estimate the creep life of a material containing wedge cracks. The model considers that failure occurs when the crack opening displacement at the tip attains a critical level and the predictions are compared with experimentally determined stress rupture relationships. © 1969 Taylor & Francis Group, LLC.

引用

页码：635 / &

共 17 条

[1]

[Anonymous], 70 IR STEEL I

[2]

BETTERIDGE W, 1958, NIMONIC ALLOYS

[3]

BILBY BA, 1963, P R SOC A, V272, P34

[4]

COTTRELL AH, 1958, T AIMME, V212, P191

[5]

COTTRELL AH, 1961, 70 IR STEEL I LOND S, P1

[6]

DAVIES PWD, 1961, 70 IR STEEL I I MET, P34

[7] MECHANISM FOR VISCOUS GRAIN-BOUNDARY SLIDING [J].

GIFKINS, RC ;

SNOWDEN, KU .

NATURE, 1966, 212 (5065) :916-&

[8]

GREENWOOD GW, 1959, PHILOS MAG, V8, P707

[9]

MONKMAN FC, 1956, P AM SOC TEST MATER, V56, P28

[10]

Tetelman AlanS., 1967, FRACTURE STRUCTURAL

← 1 2 →