LOW TEMPERATURE RECOVERY OF AL-ZN ALLOYS COLD-WORKED AT - 195DEGREES C

被引：3

作者：

CERESARA, S

机构：

[1] I.S.M.L., Novara

来源：

PHILOSOPHICAL MAGAZINE | 1968年 / 17卷 / 150期

关键词：

D O I：

10.1080/14786436808223205

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The resistivity recovery after cold-work at -195°C of a set of Al-Zn alloys, with Zn content ranging from 0 to 3.99 wt. %, is investigated by isochronal annealing procedure. Results agree with a previously discussed recovery model assuming vacancy migration in stage III. © 1968 Taylor & Francis Group, LLC.

引用

页码：1299 / &

共 7 条

[1] INFLUENCE OF AMOUNT OF STRAIN AT 78 DEGREES K ON RECOVERY PROCESS IN AL 99.995 PERCENT
CERESARA, S
ELKHOLY, H
FEDERIGHI, T
[J]. PHILOSOPHICAL MAGAZINE, 1965, 12 (120) : 1105 - +
[2] RESISTIVITY INCREASE IN POLYCRYSTALLINE AL HEAVILY COLD-WORKED AT 78 DEGREESK
CERESARA, S
ELKHOLY, H
FEDERIGH.T
[J]. PHYSICA STATUS SOLIDI, 1965, 8 (02): : 509 - &
[3] PRE-PRECIPITATION RATE IN AL-10 PERCENT ZN ALLOY NEUTTRON-IRRADIATED AT 78 DEGREES K
CERESARA, S
PIERAGOSTINI, F
FEDERIGHI, T
[J]. PHILOSOPHICAL MAGAZINE, 1964, 9 (100): : 623 - &
[4] ENHANCED PRE-PRECIPITATION RATE IN AL-ZN 10 PERCENT ALLOY BY PLASTIC DEFORMATION AT 78 DEGREES K
FEDERIGHI, T
CERESARA, S
[J]. PHILOSOPHICAL MAGAZINE, 1963, 8 (92): : 1417 - &
[5] FEDERIGHI T, 1965, LATTICE DEFECTS QUEN, P217
[6] FROIS C, 1966, ACTA METALL MATER, V14, P1325
[7] LOW-TEMPERATURE RECOVERY OF DEFORMED ALUMINUM
SWANSON, ML
[J]. CANADIAN JOURNAL OF PHYSICS, 1964, 42 (10) : 1890 - &

← 1 →