MAGNETIC REORIENTATION TRANSITION OF GD(0001)/W(110) FILMS

The temperature-dependent magnetic properties of Gd(0001)/W(110) films were investigated using the magneto-optical Kerr effect. Measurements of hysteresis loops, remanent magnetization, and susceptibility were performed as a function of temperature and film thickness (d = 10-130 nm). Well annealed films of sufficient thickness (d greater than or equal to 40 nm) show an anomalous temperature dependence of the coercive field H-c(T) and the remanent magnetization M(r)(T). In addition, a second peak in the in-plane as well as out-of-plane susceptibility was observed for these films. All experimental results for thick films can consistently be explained by a reorientation transition between a low-temperature phase with uniform inplane magnetization and a high-temperature phase with ii nonvanishing out-of-plane magnetization component. The thickness dependence of the transition temperature T-r, as well as the absence of a remanent out-of-plane magnetization implies that the reorientation transition is associated with the formation of a domain structure.