EFFECT OF SINTERING ON THE MAGNETIZATION BEHAVIOR OF MGXZN(1-X)FE2O4 SYSTEM

被引：14

作者：

PATIL, SH

PATIL, SI

KADAM, SM

PATIL, SR

CHOUGULE, BK

机构：

[1] Department of Physics, Shivaji University, Kolhapur

来源：

BULLETIN OF MATERIALS SCIENCE | 1991年 / 14卷 / 05期

关键词：

MAGNETIZATION; MG-ZN FERRITES; SINTERING;

D O I：

10.1007/BF02744616

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Magnesium zinc ferrites with the general formula MgxZn(1-x)Fe2O4 were prepared by the standard ceramic technology route involving double sintering. X-ray analysis was carried out to confirm the single-phase formation as well as to calculate the lattice parameters. Two sets of samples were prepared by sintering the samples at 1100-degrees-C for 15 and 30 h respectively. The high-field loop tracer was used to measure the hysteresis parameters. It is observed that the sintering conditions effectively modify the magnetization characteristics of these ferrites.

引用

页码：1225 / 1230

页数：6

共 21 条

[1]

Broese van Groenou A., Bongers P.F, Stuijts A.L, Mater. Sci. Engg., 3, (1968)

[2]

Evans B.J, Hafnes S.S, J. Phys. Chem. Solids, 29, (1969)

[3]

Gorter E.W, Philips Res. Rep., 9, (1954)

[4]

Igarasi H., Okazaki K., Effects of Porosity and Grain Size on the Magnetic Properties of NiZn Ferrite, Journal of the American Ceramic Society, 60, (1977)

[5]

Jain G.C, Das B.K, Khanduja R.S, Gupta G.C, J. Mater. Sci., 11, (1976)

[6]

Jain G.C, Das B.K, Tripathi R.B, Narayan R., J. Mater. Sci., 18, (1983)

[7]

Jonker G.H, Stuijts A.L, Philips Tech. Rev., 32, (1971)

[8]

Josyulu O.S, Sobhanadri J., Narayanaswamy A., Nagarajan T., Indian J. Pure Appl. Phys., 20, (1982)

[9]

Kulkarni R.G, Joshi H.H, Solid State Commun., 53, (1985)

[10]

Kulkarni R.G, Patil V.U, J. Mater. Sci., 17, (1972)

← 1 2 3 →