INITIAL-STAGES OF RECRYSTALLIZATION IN ALUMINUM OF COMMERCIAL PURITY

被引:82
作者
BAY, B [1 ]
HANSEN, N [1 ]
机构
[1] RISO NATL LAB,DEPT MET,DK-4000 ROSKILDE,DENMARK
来源
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1979年 / 10卷 / 03期
关键词
D O I
10.1007/BF02658335
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In commercial aluminum with a purity of 99.4 pct, the formation and growth of recrystallization nuclei were studied by techniques such as in-situ annealing in a high voltage electron microscope, transmission electron microscopy and light microscopy. Sample parameters were the initial grain size (370 and 19 microns) and the degree of deformation (50 and 90 pct reduction in thickness by cold-rolling). It was found that the initial grain boundaries and high angle boundaries within the original grains are preferential sites for recrystallization nuclei, and that the effect of such sites is enhanced by the FeAl3 particles present in the commercial aluminum as impurities. The nucleation temperatures determined by high voltage electron microscopy and transmission electron microscopy decrease markedly when the initial grain size is decreased both after 50 and 90 pct cold rolling; a less pronounced temperature decrease is obtained by increasing the degree of deformation. The size of the recrystallization nuclei, the recrystallization temperature and the recrystallized grain size are reported for the four sample states, and finally the structural and kinetic observations are discussed. © 1979 American Society for Metals and the Metallurgical Society of AIME.
引用
收藏
页码:279 / 288
页数:10
相关论文
共 31 条
  • [1] ANDERSON WA, 1945, T AM I MIN MET ENG, V161, P140
  • [2] STRAIN INDUCED GRAIN BOUNDARY MIGRATION IN HIGH PURITY ALUMINUM
    BECK, PA
    SPERRY, PR
    [J]. JOURNAL OF APPLIED PHYSICS, 1950, 21 (02) : 150 - 152
  • [3] STRUCTURE OF DEFORMED ALUMINUM AND ITS RECRYSTALLIZATION - INVESTIGATIONS WITH TRANSMISSION KOSSEL DIFFRACTION
    BELLIER, SP
    DOHERTY, RD
    [J]. ACTA METALLURGICA, 1977, 25 (05): : 521 - 538
  • [4] WORK-HARDENING OF COPPER-SILICA .2. ROLE OF PLASTIC RELAXATION
    BROWN, LM
    STOBBS, WM
    [J]. PHILOSOPHICAL MAGAZINE, 1971, 23 (185): : 1201 - &
  • [5] CORTI CW, 1973, M RECRYSTALLIZATION
  • [6] RECRYSTALLIZATION INDUCED BY ELECTRON-IRRADIATION OF DEFORMED NICKEL
    DAS, G
    MITCHELL, TE
    [J]. SCRIPTA METALLURGICA, 1974, 8 (10): : 1135 - 1140
  • [7] Doherty R., 1964, T ASM, V57, P874
  • [8] DOHERTY RD, 1962, J I MET, V91, P332
  • [9] ENGLISH AT, 1964, T METALL SOC AIME, V230, P396
  • [10] Fisher S. B., 1970, Radiation Effects, V5, P239, DOI 10.1080/00337577008235027