STACKING FAULTS IN THETA' PRECIPITATE OF AL-CU ALLOY

被引:2
作者
KAJIWARA, S
机构
[1] National Research Institute for Metals, Tokyo, 2-3-12, Nakameguro, Meguro-ku
关键词
D O I
10.1143/JPSJ.26.339
中图分类号
O4 [物理学];
学科分类号
0702 ;
摘要
Lattice defects in θ′ precipitate of Al-Cu alloy have been studied by electron microscopy. The fine striations are observed in the as-aged precipitates, which have so far been believed to be found only in the specimens subjected to plastic deformation. It is concluded that these striations in the electron microscope image are due to stacking faults on {101}θ′ plane. A possible displacement vector of the stacking faults is suggested to be 1/12 < a, a, c,>. It is considered that these stacking faults are produced in the θ′ precipitates during aging. The stacking fault density is different from precipitate to precipitate. © 1969, THE PHYSICAL SOCIETY OF JAPAN. All rights reserved.
引用
收藏
页码:339 / &
相关论文
共 11 条
[1]   A KINEMATICAL THEORY OF DIFFRACTION CONTRAST OF ELECTRON TRANSMISSION MICROSCOPE IMAGES OF DISLOCATIONS AND OTHER DEFECTS [J].
HIRSCH, PB ;
HOWIE, A ;
WHELAN, MJ .
PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1960, 252 (1017) :499-&
[2]  
HIRSCH PB, 1965, ELECTRON MICROS, P202
[3]  
KODA S, 1962, J I MET, V91, P229
[4]  
KODA S, 1963, J AUST I MET, V8, P197
[5]  
MATSUURA K, 1964, SCI REP RES TOHOKU A, V16, P151
[6]  
Matsuura K., 1963, J PHYS SOC JAPAN, V18, P50
[7]  
Preston GD, 1938, PHILOS MAG, V26, P855
[8]  
Silcock J.M., 1953, J I MET, V82, P239
[9]   ELECTRON DIFFRACTION FROM CRYSTALS CONTAINING STACKING FAULTS .2. [J].
WHELAN, MJ ;
HIRSCH, PB .
PHILOSOPHICAL MAGAZINE, 1957, 2 (23) :1303-&
[10]   ELECTRON DIFFRACTION FROM CRYSTALS CONTAINING STACKING FAULTS .1. [J].
WHELAN, MJ ;
HIRSCH, PB .
PHILOSOPHICAL MAGAZINE, 1957, 2 (21) :1121-1142