ELECTRODE-REACTION AT FIXED PLATINUM FILM - FIXATION OF PLATINUM FILM ON STABILIZED-ZIRCONIA ELECTROLYTE AND ITS EFFECT ON THE ELECTRODE PERFORMANCE OF THE SOLID-ELECTROLYTE FUEL-CELL

被引:3
作者
NAKAGAWA, N
KURODA, C
ISHIDA, M
机构
[1] Research Laboratory of Resources Utilization, Tokyo Institute of Technology, Yokohama, Nagatsuta 4259, Midoriku
关键词
ELECTRODE REACTION; PLATINUM FILM; ZIRCONIA; SOLID OXIDE; FUEL CELL; IMPEDANCE; ANNEALING; FIXATION;
D O I
10.1252/jcej.25.55
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
Reliable polarization characteristics of noble metal or oxide electrodes in contact with solid oxide electrolyte are quite important. To obtain such characteristics, we fixed sputtered platinum electrodes on yttria stabilized-zirconia (YSZ) electrolyte by covering the electrode with a porous ceramic layer. As a result of the fixation, the Pt film was kept stable and the resistance of the electrodes was very small. Electrode impedance and potential-current curves were measured on the fixed electrodes. The effect of the oxygen partial pressure, P(O2), on the electrode resistance, R(i), which was obtained from the impedance plots, was represented as R(i) is-proportional-to P(O2)-1 at high temperature and low oxygen partial pressure, and as R(i) is-proportional-to P(O2)1/4 at low temperature and high oxygen partial pressure. Furthermore, effects of the thickness of the Pt film and the ceramic layer on the polarization characteristics were examined. The cathodic current increased as the Pt thickness decreased. The anodic current increased as the ceramic layer thickness decreased.
引用
收藏
页码:55 / 61
页数:7
相关论文
共 21 条
[1]   IMPEDANCE SPECTROSCOPY OF THE PT YTTRIA DOPED CERIA INTERFACE [J].
BADWAL, SPS ;
DEBRUIN, HJ ;
FRANKLIN, AD .
SOLID STATE IONICS, 1983, 9-10 (DEC) :973-977
[2]   STUDY OF SOLID ELECTROLYTE POLARIZATION BY A COMPLEX ADMITTANCE METHOD [J].
BAUERLE, JE .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1969, 30 (12) :2657-&
[3]   PLATINUM ELECTRODES AND CALCIA-STABILIZED ZIRCONIA - RELATION BETWEEN ELECTRODE PROCESSES AND ELECTRODE STRUCTURE [J].
BROOK, RJ ;
PELZMANN, WL ;
KROGER, FA .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1971, 118 (02) :185-+
[4]   OVERPOTENTIAL BEHAVIOR OF STABILIZED ZIRCONIA SOLID ELECTROLYTE FUEL CELLS [J].
ETSELL, TH ;
FLENGAS, SN .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1971, 118 (12) :1890-&
[5]  
GUR TM, 1980, J ELECTROCHEM SOC, V27, P2620
[6]   COMPARISON OF MATERIALS AS OXYGEN CATALYTIC ELECTRODES ON ZIRCONIA ELECTROLYTE [J].
ISAACS, HS ;
OLMER, LJ .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1982, 129 (02) :436-443
[7]   ELECTRODE-REACTION AT PT,O-2(G)/STABILIZED ZIRCONIA INTERFACES .1. THEORETICAL CONSIDERATION OF REACTION MODEL [J].
MIZUSAKI, J ;
AMANO, K ;
YAMAUCHI, S ;
FUEKI, K .
SOLID STATE IONICS, 1987, 22 (04) :313-322
[8]   ELECTRODE-REACTION AT PT,O-2(G)/STABILIZED ZIRCONIA INTERFACES .2. ELECTROCHEMICAL MEASUREMENTS AND ANALYSIS [J].
MIZUSAKI, J ;
AMANO, K ;
YAMAUCHI, S ;
FUEKI, K .
SOLID STATE IONICS, 1987, 22 (04) :323-330
[9]   ELECTRODE PERFORMANCE OF A THIN-FILM YSZ CELL SET ON A POROUS CERAMIC SUBSTRATE BY RF SPUTTERING TECHNIQUE [J].
NAKAGAWA, N ;
YOSHIOKA, H ;
KURODA, C ;
ISHIDA, M .
SOLID STATE IONICS, 1989, 35 (3-4) :249-255
[10]  
NAKAGAWA N, 1988, NENRYO KYOKAISHI, V67, P846