MICROSTRUCTURE OF ALUMINA-FORMING OXIDATION-RESISTANT AL-TI-CR ALLOYS

被引:44
作者
BRADY, MP
SMIALEK, JL
TEREPKA, F
机构
[1] NASA Lewis Research Cent, Cleveland, OH, United States
来源
SCRIPTA METALLURGICA ET MATERIALIA | 1995年 / 32卷 / 10期
关键词
D O I
10.1016/0956-716X(95)00251-P
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
1. 1) The protective alumina-forming Al-Ti-Cr alloys identified by Perkins et al. [2] are based primarily on the τ (L12) and TiCrAl laves phases. 2. 2) The τ phase in the multiphase protective alumina-forming Al-Ti-Cr alloys is not stable at 1073K and decomposes to r-Al2Ti and Cr2Al. 3. 3) Future coating alloy development in the Al-Ti-Cr system should focus on the γ/TiCrAl laves two phase field. © 1995.
引用
收藏
页码:1659 / 1664
页数:6
相关论文
共 17 条
[1]  
BRADY MP, 1994, IN PRESS HIGH TEMPER
[2]  
Hayes FH., 1992, J PHASE EQUILIB, V13, P79, DOI [10.1007/BF02645384, DOI 10.1007/BF02645384]
[3]   STRUCTURE/PROPERTY OBSERVATIONS FOR AL-TI-CR INTERMETALLIC ALLOYS [J].
KLANSKY, JL ;
NIC, JP ;
MIKKOLA, DE .
JOURNAL OF MATERIALS RESEARCH, 1994, 9 (02) :255-258
[4]  
KUMAR KS, 1993, STRUCTURAL INTERMETALLICS, P87
[5]   ALUMINIDE COATINGS ON TIAL COMPOUND [J].
MABUCHI, H ;
ASAI, T ;
NAKAYAMA, Y .
SCRIPTA METALLURGICA, 1989, 23 (05) :685-689
[6]  
MARBUCHI H, 1990, SCRIPTA METALL MATER, V24, P505
[7]   THE OXIDATION BEHAVIOR OF GAMMA-TITANIUM ALUMINIDE ALLOYS UNDER THERMAL CYCLING CONDITIONS [J].
MCKEE, DW ;
HUANG, SC .
CORROSION SCIENCE, 1992, 33 (12) :1899-1914
[8]  
MEIER GH, 1993, STRUCTURAL INTERMETA, P869
[9]  
MEIER GH, 1991, GE1 AIRCR ENG INT RE
[10]   FORMATION OF TERNARY L12 COMPOUNDS IN AL3TI-BASE ALLOYS [J].
NAKAYAMA, Y ;
MABUCHI, H .
INTERMETALLICS, 1993, 1 (01) :41-48