EFFECT OF COPPER CONTENT AND DEGREE OF RECRYSTALLIZATION ON THE FATIGUE RESISTANCE OF 7XXX-TYPE ALUMINUM-ALLOYS .1. LOW-CYCLE CORROSION FATIGUE

被引:50
作者
LIN, FS
STARKE, EA
机构
[1] Fracture and Fatigue Research Laboratory, Georgia Institute of Technology, Atlanta
来源
MATERIALS SCIENCE AND ENGINEERING | 1979年 / 39卷 / 01期
关键词
D O I
10.1016/0025-5416(79)90167-8
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The effect of copper content (0.01-2.1%) and degree of recrystallization (DR) (5-45%) on the corrosion fatigue behavior of four AlZn2MgxCuT651 alloys was investigated. The cyclic strain resistance was found to increase with copper content and decrease with DR regardless of the test environment. This trend is more pronounced in aggressive environments. The improved fatigue resistance is attributed to the increased homogeneity of slip as the copper content is increased and the DR is decreased. The environmental sensitivity, which increases with decreasing copper content, is dependent on slip behavior. For alloys tested in distilled water hydrogen embrittlement is believed to be the major factor controlling the low cycle corrosion fatigue. For tests conducted in a 3.5% NaCl solution hydrogen embrittlement still plays an important role but the preferential dissolution and/or adsorption process may also have a detrimental effect. © 1979.
引用
收藏
页码:27 / 41
页数:15
相关论文
共 47 条
[1]   AGING PHENOMENA AND LATTICE DEFECTS IN AL-ZN AND AL-ZN-MG ALLOYS [J].
BABA, Y .
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1966, 7 (04) :224-&
[2]   CHANGES IN INFLUENCE OF ATMOSPHERIC HUMIDITY DURING FATIGUE OF ALUMINUM ALLOY [J].
BENNETT, JA .
JOURNAL OF RESEARCH OF THE NATIONAL BUREAU OF STANDARDS SECTION C-ENGINEERING AND INSTRUMENTATION, 1964, C 68 (02) :91-+
[3]  
BOETTNER RC, 1965, T METALL SOC AIME, V233, P379
[4]   ROLE OF INCLUSIONS IN FATIGUE CRACK INITIATION IN AN ALUMINUM-ALLOY [J].
BOWLES, CQ ;
SCHIJVE, J .
INTERNATIONAL JOURNAL OF FRACTURE, 1973, 9 (02) :171-179
[5]  
BRADSHAW FJ, 1969, INT J FRACTURE, V5, P255
[6]  
BRADSHAW FJ, 1966, APPL MATER RES, V5, P112
[7]  
Broom T.NicholsonA, 1960, J I MET, V89, P183
[8]   HIGH STRAIN FATIGUE FRACTURE MECHANISMS IN 2 PHASE ALLOYS [J].
CALABRESE, C ;
LAIRD, C .
METALLURGICAL TRANSACTIONS, 1974, 5 (08) :1785-1793
[9]  
COFFIN LF, 1971, J MATER, V6, P388
[10]  
Cotterill P., 1976, RECRYSTALLIZATION GR