STRESS-STRAIN RELATIONS OF HFIR-IRRADIATED AUSTENITIC STAINLESS-STEELS

被引:14
作者
JITSUKAWA, S [1 ]
GROSSBECK, ML [1 ]
HISHINUMA, A [1 ]
机构
[1] OAK RIDGE NATL LAB,DIV MET & CERAM,OAK RIDGE,TN 37831
关键词
D O I
10.1016/0022-3115(91)90150-6
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Tensile specimens of austenitic stainless steels were irradiated up to 50 dpa at temperature of 573, 673 and 773 K and HFIR. True stress-strain relation derived from the load-displacement curves were analyzed in terms of induced effective strain and strain hardening behavior. The strain hardening exponent of the material was only slightly affected by irradiation at 573 and 673 K. Irradiation at 773 K changes work hardening characteristics. This might have resulted from fine MC precipitation and/or helium produced during irradiation. Fracture strain decreases with dose, and the dose dependence was pronounced at 773 K. Heat-to-heat variation was not large between two Ti-modified steels.
引用
收藏
页码:563 / 567
页数:5
相关论文
共 9 条
[1]  
DEVRIES MI, 1972, IRRADIATION EMBRITTL, P47
[2]  
GARR KR, 1976, ASTM STP, V611, P72
[3]  
GROSSBECK ML, 1989, ADIP DOEER03136 ORNL, P259
[4]  
GROSSBECK ML, 1991, J NUCL MATER, V179
[5]   RADIATION-DAMAGE OF HFIR-IRRADIATED CANDIDATE STAINLESS-STEELS FOR FUSION APPLICATIONS [J].
HISHINUMA, A ;
JITSUKAWA, S .
JOURNAL OF NUCLEAR MATERIALS, 1989, 169 :241-248
[6]  
MELLOR PB, 1956, J MECH PHYS SOLIDS, V5, P5
[7]  
PUGH HLD, 1964, ASTM STP, V374, P68
[8]  
ROWCLIFFE AF, 1984, ADIP DOEER004512 ORN, P38
[9]   POST IRRADIATION TENSILE AND FATIGUE BEHAVIOR OF AUSTENITIC PCA STAINLESS-STEELS IRRADIATED IN HFIR [J].
TANAKA, MP ;
HAMADA, S ;
HISHINUMA, A ;
GROSSBECK, ML .
JOURNAL OF NUCLEAR MATERIALS, 1988, 155 (pt B) :957-962