EFFECTS OF INTERFACIAL CONDITIONS ON WALL SLIP AND SHARKSKIN MELT FRACTURE OF HDPE

被引:74
作者
HATZIKIRIAKOS, SG [1 ]
DEALY, JM [1 ]
机构
[1] MCGILL UNIV,DEPT CHEM ENGN,MONTREAL H3A 2T5,QUEBEC,CANADA
关键词
D O I
10.3139/217.930036
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
Experiments were performed in capillary and slit rheometers to determine the effects of the presence of fluoropolymers at the polymer-wall interface on wall slip and extrudate distortion of a molten high density polyethylene. Two fluoropolymers were used to modify the interface. It was found that one of these decreased slip compared to the clean interface while the other increased slip. However, both were found to improve extrudate appearance, thus indicating that both adhesion promoters and slip promoters may improve extrudate appearance. The mechanism underlying this rather surprising conclusion is also discussed.
引用
收藏
页码:36 / 44
页数:9
相关论文
共 19 条
  • [1] [Anonymous], 1987, FLUID MECH-SOV RES
  • [2] ATHEY RJ, 1986, SPE ANTEC TECH PAPER, V32, P1149
  • [3] CHARACTERIZATION OF THE SHARKSKIN DEFECT AND ITS DEVELOPMENT WITH THE FLOW CONDITIONS
    BEAUFILS, P
    VERGNES, B
    AGASSANT, JF
    [J]. INTERNATIONAL POLYMER PROCESSING, 1989, 4 (02) : 78 - 84
  • [4] BERGEM N, 1976, 7TH P INT C RHEOL GO, P50
  • [5] COGSWELL FN, 1981, POLYM MELT RHEOLOGY, P101
  • [6] Dealy J., 1990, MELT RHEOLOGY ITS RO
  • [7] ROLE OF SLIP AND FRACTURE IN THE OSCILLATING FLOW OF HDPE IN A CAPILLARY
    HATZIKIRIAKOS, SG
    DEALY, JM
    [J]. JOURNAL OF RHEOLOGY, 1992, 36 (05) : 845 - 884
  • [8] WALL SLIP OF MOLTEN HIGH-DENSITY POLYETHYLENES .2. CAPILLARY RHEOMETER STUDIES
    HATZIKIRIAKOS, SG
    DEALY, JM
    [J]. JOURNAL OF RHEOLOGY, 1992, 36 (04) : 703 - 741
  • [9] WALL SLIP OF MOLTEN HIGH-DENSITY POLYETHYLENE .1. SLIDING PLATE RHEOMETER STUDIES
    HATZIKIRIAKOS, SG
    DEALY, JM
    [J]. JOURNAL OF RHEOLOGY, 1991, 35 (04) : 497 - 523
  • [10] WALL SLIP AND EXTRUDATE DISTORTION IN LINEAR LOW-DENSITY POLYETHYLENE
    KALIKA, DS
    DENN, MM
    [J]. JOURNAL OF RHEOLOGY, 1987, 31 (08) : 815 - 834