EFFECTS OF NANOCRYSTALLIZATION UPON THE SOFT-MAGNETIC PROPERTIES OF CO-BASED AMORPHOUS-ALLOYS

Amorphous samples of Vitrovac(R) 6025 metallic alloys were nanocrystallized by thermal annealing at temperatures in the range 576-716 K, well below the crystallization temperature (831 K, as obtained by differential scanning calorimetry at 20 K/min) and times in the range 10-90 min. Initial magnetic permeability exhibited a maximum of ∼109 000 (from ∼20 000 for the as-quenched state) for annealing times of ∼15 min, and then a decrease toward a plateau value (30 000-40 000) for longer times. Domain wall relaxation frequency showed the opposite behavior, a minimum of ∼9 kHz (from 40 kHz for the as-quenched value) for the permeability maximum, and then a stabilization at ∼15 kHz. Transmission electron microscopy observations confirmed that for annealing times up to 60 min., crystallite size is smaller than 30 nm. Permeability and relaxation frequency results are interpreted in terms of the dependence of wall bulging on anisotropy and free-wall surface area between pinning sites.