MECHANICAL-PROPERTIES OF QUASI-CRYSTALLINE AND CRYSTALLINE PHASES IN AL-CU-FE ALLOYS

被引：149

作者：

KOSTER, U

LIU, W

LIEBERTZ, H

MICHEL, M

机构：

[1] Department of Chemical Engineering, University of Dortmund

来源：

JOURNAL OF NON-CRYSTALLINE SOLIDS | 1993年 / 153卷

关键词：

Aluminum copper iron alloys - Icosahedral quasicrystals - Indentation - Plastic deformation - Three point bending;

D O I：

10.1016/0022-3093(93)90393-C

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Mechanical properties of icosahedral AlCuFe quasicrystals were investigated and compared with those of related crystalline intermetallic compounds by means of indentation and three-point bending techniques. Quasicrystalline phases possess high hardness (HV almost-equal-to 1000) and high ability for elastic recovery (H/E > 0.08) but exhibit low toughness against unstable fracture (K(IC) almost-equal-to 1 MPa m1/2). Icosahedral particles embedded in Al2Cu or in AlFe crystalline matrices lead to increasing resistance against subcritical crack propagation. In contrast to cleavage #1 fracture in crystalline Al13Fe4, the icosahedral quasicrystals exhibit a rough, quasicleavage #1 fracture surface. Evidences for plastic deformation in the quasicrystals were found and its mechanism is discussed.

引用

页码：446 / 452

页数：7

共 11 条

[1]

BHADURI SB, 1987, NATURE, V37, P609

[2] QUASI-CRYSTALLINE LOW-FRICTION COATINGS [J].

DUBOIS, JM ;

KANG, SS ;

VONSTEBUT, J .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1991, 10 (09) :537-541

[3]

KLEINLEIN FW, 1978, ADV RES STRENGTH FRA, P883

[4]

LAWN BR, 1981, J MATER SCI, V16, P2745, DOI 10.1007/BF02402837

[5]

MICHEL M, 1992, THESIS U DORTMUND

[6] EVALUATION OF KLC OF BRITTLE SOLIDS BY THE INDENTATION METHOD WITH LOW CRACK-TO-INDENT RATIOS [J].

NIIHARA, K ;

MORENA, R ;

HASSELMAN, DPH .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1982, 1 (01) :13-16

[7]

SAINFORT P, 1988, QUASICRYSTALLINE MAT, P361

[8] PLASTIC-DEFORMATION OF AL-RU-CU ICOSAHEDRAL QUASI-CRYSTALS [J].

SHIBUYA, T ;

HASHIMOTO, T ;

TAKEUCHI, S .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1990, 29 (02) :L349-L351

[9] ELASTIC-MODULUS VERSUS MELTING TEMPERATURE IN ALUMINUM BASED INTERMETALLICS [J].

SKINNER, DJ ;

ZEDALIS, M .

SCRIPTA METALLURGICA, 1988, 22 (11) :1783-1785

[10]

SOCOLAR JES, 1986, PHYS REV B, V34, P2245

← 1 2 →