OXIDATION BEHAVIOR OF AUSTENITIC FE-CR-NI ALLOYS CONTAINING DISPERSED PHASES

The high temperature oxidation behaviour of FeCrNi austenitic alloys containing 1% Ti which, in some cases, had been converted into an oxide dispersion has been examined. The oxide dispersions were produced by an internal oxidation treatment using a 50/50 Cr/Cr2O3 powder mixture in a sealed quartz capsule at 1100°C: the samples were not in direct contact with the powders. Generally, the effect of the dispersed oxide was much less pronounced than in corresponding nickel-free, ferritic alloys. Nevertheless, the time-to-breakaway of the protective Cr3O3 scale which developed on Fe18CrNi alloys was substantially increased, although the differences between the untreated and the internally oxidized alloys reduced with increasing nickel content. An Fe14Cr20Ni alloy did not show any improvement after internal oxidation. Unlike the ferritic alloys, no coarsening of the dispersoid phase was observed during exposure. © 1979.