A STUDY OF THE DELAMINATION RESISTANCE OF IM6/PEEK COMPOSITES

被引：57

作者：

DAVIES, P

CANTWELL, W

MOULIN, C

KAUSCH, HH

机构：

[1] Ecole Polytechnique Federale de, Lausanne, Switzerland

来源：

COMPOSITES SCIENCE AND TECHNOLOGY | 1989年 / 36卷 / 02期

关键词：

Calorimetry - Plastics Laminates--Fracture;

D O I：

10.1016/0266-3538(89)90085-7

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

This paper describes the delamination behaviour of unidirectional carbon fibre/PEEK (poly(ether ether ketone)) composites. Tests have been performed under mode I and mode II loading conditions, using double cantilever beam (DCB) and end-notched flexure (ENF) specimens. Mode I tests on specimens of different thicknesses indicated that propagation values of GIc were dependent on thickness, higher values being obtained for 5 mm than for 3 mm. This was due to increased fibre bridging and multiple crack formation in thicker specimens and may explain scatter in previously published values.

引用

页码：153 / 166

页数：14

共 21 条

[1]

BERGLUND L, 1985, THESIS LINKOPING U S

[2]

CANTWELL W, IN PRESS COMP STRUCT

[3] INTERLAMINAR FRACTURE MORPHOLOGY OF CARBON-FIBER PEEK COMPOSITES [J].

CRICK, RA ;

LEACH, DC ;

MEAKIN, PJ ;

MOORE, DR .

JOURNAL OF MATERIALS SCIENCE, 1987, 22 (06) :2094-2104

[4]

CURTIS PT, 1987, 1987 P ICCM6ECCM2 LO

[5] MEASUREMENT OF INITIATION VALUES OF GIC IN IM6/PEEK COMPOSITES [J].

DAVIES, P ;

CANTWELL, W ;

KAUSCH, HH .

COMPOSITES SCIENCE AND TECHNOLOGY, 1989, 35 (03) :301-313

[6]

DAVIES P, 1987, 1987 P ICCMLECCM2

[7]

DAVIES P, IN PRESS APPLICATION

[8]

DAVIES P, 1987, THESIS U TECHNOLOGIE

[9]

de Charentenay F., 1982, ASTM STP, V836, P84

[10] RATE-DEPENDENT MODE-I INTERLAMINAR CRACK-GROWTH MECHANISMS IN GRAPHITE-EPOXY AND GRAPHITE-PEEK [J].

GILLESPIE, JW ;

CARLSSON, LA ;

SMILEY, AJ .

COMPOSITES SCIENCE AND TECHNOLOGY, 1987, 28 (01) :1-15

← 1 2 3 →