LOW-CYCLE FATIGUE DAMAGE IN NICKEL-BASE SUPERALLOY SINGLE-CRYSTALS AT ELEVATED-TEMPERATURE

被引：87

作者：

FLEURY, E

REMY, L

机构：

[1] Centre des Matériaux P.M. Fourt, Ecole des Mines, URA CNRS 866 -, 91003 Evry

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1993年 / 167卷 / 1-2期

关键词：

D O I：

10.1016/0921-5093(93)90332-9

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Low cycle fatigue tests on AM1 nickel-base superalloy single crystals were conducted under axial strain control at 650, 950 and 1100-degrees-C. The behaviour of the [001] orientation was investigated at the three temperatures, that of the [111], [101] and [213] specimens was studied at the two lower temperatures. The orientation dependence of fatigue life-total strain range curves was mainly due to variations in Young's modulus with orientation. Most cracks grow in stage II mode whatever the temperature. Cracks nucleate at micropores and in the interior of specimens at low temperatures; surface cracks induced by oxidation are dominant at high temperatures and low strain ranges. Most of fatigue life is spent in microcrack growth.

引用

页码：23 / 30

页数：8

共 22 条

[1]

AGHION E, 1987, LOW CYCLE FATIGUE EL, P360

[2]

BOUSE GK, SUPERALLOYS 1984, P751

[3] ELEVATED-TEMPERATURE FATIGUE CRACK-GROWTH BEHAVIOR OF MAR-M200 SINGLE-CRYSTALS [J].

CHAN, KS ;

LEVERANT, GR .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (04) :593-602

[4] INFLUENCE OF ORIENTATION ON THE LOW-CYCLE FATIGUE OF MAR-M200 SINGLE-CRYSTALS AT 650-DEGREES-C .1. FATIGUE LIFE BEHAVIOR [J].

CHIERAGATTI, R ;

REMY, L .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 141 (01) :1-9

[5] CRACK-GROWTH IN A SINGLE-CRYSTAL SUPERALLOY AT ELEVATED-TEMPERATURE [J].

CROMPTON, JS ;

MARTIN, JW .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (09) :1711-1719

[6] FATIGUE BEHAVIOR OF CMSX 2 SUPERALLOY [001] SINGLE-CRYSTALS AT HIGH-TEMPERATURE .1. LOW-CYCLE FATIGUE OF NOTCHED SPECIMENS [J].

DEFRESNE, A ;

REMY, L .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1990, 129 (01) :45-53

[7]

DEFRESNE A, FATIGUE 90, V4, P2435

[8] EFFECTS OF ENVIRONMENT ON ELEVATED-TEMPERATURE FATIGUE BEHAVIOR OF NICKEL-BASE SUPERALLOY SINGLE-CRYSTALS [J].

DUQUETTE, DJ ;

GELL, M .

METALLURGICAL TRANSACTIONS, 1972, 3 (07) :1899-&

[9]

Fleury E., 1991, THESIS ECOLE MINES P

[10]

FREDHOLM A, 1987, THESIS ECOLE MINES P

← 1 2 3 →