STUDIES ON THE TEMPERATURE-DEPENDENCE OF THE ELASTIC-MODULUS OF CRYSTALLINE REGIONS OF POLYMERS .14. POLY(VINYL ALCOHOL) WITH DIFFERENT TACTICITIES

被引:30
作者
NAKAMAE, K [1 ]
NISHINO, T [1 ]
OHKUBO, H [1 ]
MATSUZAWA, S [1 ]
YAMAURA, K [1 ]
机构
[1] SHINSHU UNIV,FAC TEXT SCI & TECHNOL,UEDA 386,JAPAN
关键词
CRYSTAL MODULUS; POLY(VINYL ALCOHOL); TACTICITY; TEMPERATURE DEPENDENCE; ELASTIC MODULUS; MECHANICAL PROPERTIES;
D O I
10.1016/0032-3861(92)91141-N
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
The temperature dependence of the elastic modulus E1 of crystalline regions in the direction parallel to the chain axis has been measured by X-ray diffraction for poly (vinyl alcohol) (PVA) with different tacticities. The E1 value for PVA with 55.4% syndiotactic diads, sPVA(55.4%), decreased above 120-degrees-C, which was in accordance with that of atactic PVA. The lattice spacing for the (020) plane (the fibre axis is b) also decreased with increasing temperature. The thermal expansion coefficient alpha(c) changed discontinuously around the temperature range where E1 began to decrease. These phenomena could be explained using the kinked-chain model, where a small amount of a contracted portion, such as a kink, was incorporated into the chain molecule as in the case of atactic PVA. On the other hand, the E1 value of sPVA(63.0%) remained unchanged till 150-degrees-C. The value of alpha(c) did not change with increasing temperature in this case. Consequently, the molecular motion that is responsible for the decrement of E1 is considered to be restricted for sPVA (63.0%) because of strong intermolecular hydrogen bonds. Further, increasing the syndiotacticity is considered to be one of the most effective ways to introduce high heat resistance into PVA.
引用
收藏
页码:2581 / 2586
页数:6
相关论文
共 38 条
[1]  
KENNEY JF, 1966, J POLYM SCI A, V1, P679
[2]  
KUNUGI T, 1988, 32ND IUPAC INT S MAC, P431
[3]  
LEMSTRA PJ, 1987, DEV ORIENTED POLYM, V2, pCH2
[4]  
MATSUZAWA S, 1973, MAKROMOL CHEM, V165, P217
[5]   SURFACE-TENSION OF TACTIC POLYVINYLALCOHOLS IN WATER-DMSO-SOLUTION [J].
MATSUZAWA, S ;
UEBERREITER, K .
COLLOID AND POLYMER SCIENCE, 1978, 256 (05) :490-493
[6]   ISOTACTIC POLYVINYL ALCOHOL [J].
MURAHASHI, S ;
YUKI, H ;
SANO, T ;
TADOKORO, H ;
YONEMURA, U ;
CHATANI, Y .
JOURNAL OF POLYMER SCIENCE, 1962, 62 (174) :S77-&
[7]  
Murahashi S., 1966, KOBUNSHI KAGAKU, V23, P605
[8]  
NAGAI A, 1964, REP PROGR POLYM PHYS, V8, P249
[9]  
NAGAI E, 1956, POLYVINYL ALCOHOL, P245
[10]   TACTICITY DEPENDENCE OF MOLECULAR-MOTION IN CRYSTAL OF POLYVINYL-ALCOHOL) [J].
NAGURA, M ;
MATSUZAWA, S ;
YAMAURA, K ;
ISHIKAWA, H .
POLYMER JOURNAL, 1982, 14 (01) :69-72