PREPARATION OF FERROELECTRIC BI4TI3O12 THIN-FILMS WITH C-AXIS ORIENTATION BY ATMOSPHERIC-PRESSURE METAL-ORGANIC CHEMICAL-VAPOR-DEPOSITION

被引:41
作者
YOSHIMURA, K
ISHINABE, M
OKAMURA, S
TSUKAMOTO, T
机构
[1] Department of Applied Physics, Science University of Tokyo, Tokyo, 162, 1-3 Kagurazaka, Shinjuku-ku
来源
JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS | 1995年 / 34卷 / 5A期
关键词
THIN FILM; BI4TI3O12; MOCVD; BI(O-C7H7)(3); TI(I-OC3H7)(2)(DPM)(2); FERROELECTRICS;
D O I
10.1143/JJAP.34.2425
中图分类号
O59 [应用物理学];
学科分类号
摘要
Ferroelectric Bi4Ti3O12 thin films were prepared by the metal-organic chemical vapor deposition (MOCVD) method at atmospheric pressure using Bi(o-C7H7)(3) and Ti(i-OC3H7)(2)(DPM)(2) as metalorganic sources. Assist Ar gas flow rate effects on the growth of the thin films were also examined. Thin films obtained were characterized by XRD analysis, SEM, AFM and D-E hysteresis loop observations. Most of the single-phase Bi4Ti3O12 thin films with c-axis orientation were deposited on Pt/Ti/SiO2/Si and Pt substrates above 500 degrees C. Completely c-axis-oriented Bi4Ti3O12 thin films were prepared on Pt plates at 600 degrees C, which showed good ferroelectric properties: remanent polarization of 1.0 mu C/cm(2), coercive field of 18 kV/cm and leakage current on the order of 10(-9) A/cm(2).
引用
收藏
页码:2425 / 2429
页数:5
相关论文
共 12 条
  • [1] Toyoda M., Hamaji Y., Tomono K., Payne D.A., Jpn. J. Appi. Phys, 32, (1993)
  • [2] Masumoto H., Goto T., Masuda Y., Baba A., Hirai T., Appi. Phys. Lett, 58, (1991)
  • [3] Sugibuchi K., Kurogi Y., Endo N., J. Appi. Phys, 46, (1975)
  • [4] Buhay H., Sinharoy S., Kasner W.H., Francombe M.H., Lampe D.R., Stepke E., Appi. Phys. Lett, 58, (1991)
  • [5] Maffei N., Kmpanidhi S.B., Appi. Phys. Lett, 60, (1992)
  • [6] Kakimi A., Okamura S., Yagi Y., Mori K., Tsukamoto T., Jpn. J. Appi. Phys, 33, (1994)
  • [7] Kakimi A., Okamura S., Tsukamoto T., Jpn. J. Appi. Phys, 33, (1994)
  • [8] Nakamura T., Muhammet R., Shimizu M., Shiosaki T., Jpn. J. Appi. Phys, 32, (1993)
  • [9] Masumoto H., Namerikawa M., Hirai T., Proc. First Conf. Processing Materials for Properties, (1993)
  • [10] Yoshimura K., Okamura S., Tsukamoto T., J. Ceram. Soc. Jpn, 102, (1994)