ANTIBACTERIAL ACTIVATED CARBON-FIBER DERIVED FROM METHYL METHACRYLATE-GRAFTED PHENOLIC RESIN FIBER

被引：16

作者：

OYA, A

KIMURA, M

SUGO, T

KATAKAI, A

ABE, Y

IIZUKA, T

MAKIYAMA, N

LINARESSOLANO, A

DELECEA, CS

机构：

[1] JAPAN ATOM ENERGY RES INST,TAKASAKI,GUNMA 37012,JAPAN

[2] GUNEI CHEM IND CO LTD,TAKASAKI,GUNMA 370,JAPAN

[3] UNIV ALICANTE,FAC SCI,ALICANTE,SPAIN

来源：

CARBON | 1994年 / 32卷 / 01期

关键词：

ANTIBACTERIAL ACTIVITY; ACTIVATED CARBON FIBER; WATER PURIFIER; SILVER; GRAFT-POLYMERIZATION;

D O I：

10.1016/0008-6223(94)90015-9

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Methyl methacrylate-grafted phenolic resin fiber was soaked in AgNO3 aqueous solution to support Ag+ by ion exchange reaction. The fiber supporting Ag+ was carbonized at 900-degrees-C for 30 min in a nitrogen atmosphere, followed by activation at 900-degrees-C under a stream of steam. One of the activated fibers contained 0.58 wt% of silver and showed 2100 m2/g of Specific surface area and 200 MPa of tensile strength. This fiber showed antibacterial activity against Staphylococcus aureus and Escherichia coli before and after soaking in the flowing tap water for 20 days. The amount of Ag+ dissolved from the fiber into the water is discussed from a viewpoint of practical use.

引用

页码：107 / 110

页数：4

共 9 条

[1] Gregg S.J., 1982, ADSORPTION SURFACE A, P42
[2] HAYES FS, 1981, KIRK OTHMER ENCY CHE, V16, P125
[3] METHOD FOR THE CALCULATION OF EFFECTIVE PORE-SIZE DISTRIBUTION IN MOLECULAR-SIEVE CARBON
HORVATH, G
KAWAZOE, K
[J]. JOURNAL OF CHEMICAL ENGINEERING OF JAPAN, 1983, 16 (06) : 470 - 475
[4] HOZUMI K, 1965, ORGANIC QUANTITATIVE, P68
[5] IKESHIMA S, 1986, JETI, V34, P73
[6] MATSUO T, 1977, SEN-I GAKKAISHI, V33, P204
[7] MIYAMOTO M, 1960, BUNSEKI KAGAKU, V9, P869
[8] Oya A., 1991, Applied Clay Science, V6, P135, DOI 10.1016/0169-1317(91)90003-R
[9] ANTIBACTERIAL ACTIVATED CARBON-FIBER DERIVED FROM PHENOLIC RESIN FIBER BY USE OF CO-GRAFTPOLYMERIZATION
OYA, A
KIMURA, M
SUGO, T
KATAKAI, A
ABE, Y
IIZUKA, T
MAKIYAMA, N
[J]. JOURNAL OF MATERIALS SCIENCE, 1993, 28 (17) : 4731 - 4734

← 1 →