SMALL-ANGLE X-RAY-SCATTERING STUDY OF POLYETHYLENE FIBERS, USING THE 2-DIMENSIONAL CORRELATION-FUNCTION

By Fourier transformation of the intensity distribution in the small angle X-ray scattering diagram of a polymer fibre one obtains the corresponding two-dimensional correlation function. This is compared with correlation functions calculated on the basis of different models of the semi-crystalline morphology. Here, two steps may be distinguished: in the first, the correctness of a model may be checked with the aid of qualitative features, such as the relative positions and sizes of positive and negative areas; in the second a quatitative agreement is pursued by fixing the various parameters involved. This method was applied to cold drawn low density polyethylene before and after annealing at different temperatures. In the case of the non-annealed sample, the microparacrystalline model, discussed by Hosemann and Loboda-Cackovic (J. Appl. Cryst. 11, 540 (1978)) was found to give the best fit. Annealing at 80 °C or higher temperatures seems to lead to what has been indicated as a three-dimensional chess-board structure; it consists of fibrils in which crystalline and amorphous regions alternate in such a way that the crystalline regions in a fibril are adjacent to amorphous regions in neighbouring fibrils. © 1979 Dr. Dietrich Steinkopff Verlag.