PLASMA-MODIFIED NYLON-4 MEMBRANES FOR REVERSE-OSMOSIS DESALINATION

被引:25
作者
LAI, JY
CHAO, YC
机构
[1] Department of Chemical Engineering, Chung Yuan University, Chung Li
关键词
D O I
10.1002/app.1990.070391109
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
The effects of maturation time of casting solution and annealing conditions on reverse osmosis (RO) properties of nylon 4 membranes are studied. The effects of plasma treatment conditions, such as supply power, treatment time, and gases used in reactor, on the water contact angle, surface energy, water flux, and salt rejection of nylon 4 membranes are considered. The best results of 4.86 × 10−5 g/cm2 s of water flux with 74.2% of salt rejection for 1 wt % NaCl aqueous feed solution can be obtained in the conditions of plasma treatment for 80 W–3 min in a reactor with O2 on 25 wt % formic acid–4 h annealing nylon 4 membranes. The hydrophilic monomers, such as 1‐vinyl‐2‐pyrrolidone (VP), 2‐hydroxyethyl methacrylate (HEMA), and acrylic acid (AA), are plasma deposited onto the chemical and/or plasma etched nylon 4 membranes to improve the salt rejection without decrease in water flux. The salt rejection of 90.9% and water flux of 3.64 × 10−5 g/cm2 s of the deposited membrane are obtained in the conditions of depositing AA monomer onto the substrate membrane which was previously treated with annealing followed with plasma etching. Copyright © 1990 John Wiley & Sons, Inc.
引用
收藏
页码:2293 / 2303
页数:11
相关论文
共 23 条
[1]   GAS PLASMA TREATMENT OF POLYMER SURFACES [J].
COOPES, IH ;
GIFKINS, KJ .
JOURNAL OF MACROMOLECULAR SCIENCE-CHEMISTRY, 1982, A17 (02) :217-226
[2]   PREPARATION AND PROPERTIES OF PLASMA-DEPOSITED FILMS WITH SURFACE ENERGIES VARYING OVER A WIDE-RANGE [J].
HAQUE, Y ;
RATNER, BD .
JOURNAL OF APPLIED POLYMER SCIENCE, 1986, 32 (04) :4369-4381
[3]   GRAFTING OF ACRYLAMIDE TO NYLON-6 BY THE ELECTRON-BEAM PREIRRADIATION TECHNIQUE .5. PERMEABILITY AND SELECTIVITY OF THE GRAFTED MEMBRANES TO IONIC SOLUTES AND METABOLITES [J].
HARUVY, Y ;
RAJBENBACH, LA ;
JAGURGRODZINSKI, J .
JOURNAL OF APPLIED POLYMER SCIENCE, 1987, 33 (02) :389-400
[4]   GRAFTING OF ACRYLAMIDE TO NYLON-6 BY ELECTRON-BEAM PREIRRADIATION .4. SORPTION OF WATER IN NYLON GRAFTED ACRYLAMIDE MEMBRANES [J].
HARUVY, Y ;
RAJBENBACH, LA ;
JAGURGRODZINSKI, J .
JOURNAL OF APPLIED POLYMER SCIENCE, 1986, 32 (04) :4649-4656
[5]   SYNTHESIS OF REVERSE-OSMOSIS MEMBRANES BY PLASMA POLYMERIZATION OF ALLYLAMINE [J].
HOLLAHAN, JR ;
WYDEVEN, T .
SCIENCE, 1973, 179 (4072) :500-501
[6]   SOME EXPERIMENTAL PARAMETERS AFFECTING PERFORMANCE OF COMPOSITE REVERSE-OSMOSIS MEMBRANES PRODUCED BY PLASMA POLYMERIZATION [J].
HOLLAHAN, JR ;
WYDEVEN, T .
JOURNAL OF APPLIED POLYMER SCIENCE, 1977, 21 (04) :923-935
[7]  
HOSHINO K, 1944, CHEM SOC JPN B, V19, P156
[8]   INVESTIGATIONS ON NYLON-4 MEMBRANES - SYNTHESIS AND TRANSPORT-PROPERTIES .2. TRANSPORT-PROPERTIES OF NYLON-4 POLYMER MEMBRANES [J].
HUANG, RYM ;
KIM, UY ;
DICKSON, JM ;
LLOYD, DR ;
PENG, CY .
JOURNAL OF APPLIED POLYMER SCIENCE, 1981, 26 (06) :1907-1918
[9]   INVESTIGATIONS ON NYLON-4 MEMBRANES - SYNTHESIS AND TRANSPORT-PROPERTIES .1. SYNTHESIS OF NYLON-4 POLYMER [J].
HUANG, RYM ;
KIM, UY ;
DICKSON, JM ;
LLOYD, DR ;
PENG, CY .
JOURNAL OF APPLIED POLYMER SCIENCE, 1981, 26 (04) :1135-1142
[10]   CHEMICAL INITIATED-GRAFTED NYLON-4 MEMBRANES [J].
JONG, A ;
CHANG, TC ;
LAI, JY .
JOURNAL OF APPLIED POLYMER SCIENCE, 1988, 36 (01) :87-103