MODELING OF ORMOCER COATINGS BY PROCESSING

被引:103
作者
NASS, R [1 ]
ARPAC, E [1 ]
GLAUBITT, W [1 ]
SCHMIDT, H [1 ]
机构
[1] FRAUNHOFER INST SILICATFORSCH,W-8700 WURZBURG,GERMANY
关键词
D O I
10.1016/0022-3093(90)90160-N
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Hydrolysis, condensation and polymerization of γ-glycidyloxipropyltrimethoxysilane was studied under different reaction conditions and yields a hard coating material for polyethyleneterephthalate substrates. The progress of hydrolysis was followed by 29Si-NMR spectroscopy and Karl Fischer filtration. Hydrolysis proceeds very slowly at pH 5.5, but can be enhanced at pH 9. Independent from submitted water and pH the solutions only one half of hydrolyzable methoxy groups can be removed. Condensation and polymerization were investigated on coated substrates and start during thermal curing. The formation of the polysiloxane network takes place by elimination of methanol. Polymerization of the epoxy groups to polethyleneoxide units is achieved above 100°C using a special catalyst. The properties of the cured coatings depend on the free water and glycol content in the solution. Minimizing the amount of both components leads to an ORMOCER coating on polyethyleneterephthalate which features a good abrasion resistance in combination with a high flexibility. © 1990.
引用
收藏
页码:370 / 374
页数:5
相关论文
共 11 条
  • [1] DIRECT TITRATION OF EPOXY COMPOUNDS + AZIRIDINES
    JAY, RR
    [J]. ANALYTICAL CHEMISTRY, 1964, 36 (03) : 667 - &
  • [2] NMR-STUDY OF THE SOL-GEL POLYMERIZATION
    POUXVIEL, JC
    BOILOT, JP
    BELOEIL, JC
    LALLEMAND, JY
    [J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 1987, 89 (03) : 345 - 360
  • [3] CHEMISTRY OF MATERIAL PREPARATION BY THE SOL-GEL PROCESS
    SCHMIDT, H
    [J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 1988, 100 (1-3) : 51 - 64
  • [4] SCHMIDT H, 1986, COLLECT PAPERS, V2, P429
  • [5] Schmidt H., 1988, ULTRASTRUCTURE PROCE, P651
  • [6] SCHMIDT H, 1989, J NONCRYST SOLIDS, V80, P557
  • [7] Schmidt H., 1984, MATER RES SOC S P, V32, P327
  • [8] SCHMIDT H, 1990, IN PRESS 4TH P INT C
  • [9] SCHMIDT HK, 1988, ACS SYM SER, V360, P333
  • [10] Schmidt HK, 1988, DVS BERICHTE, V110, P54