THERMAL-DEGRADATION OF BIRCH WOOD WITH SUPERCRITICAL GASES (ORGANIC-SOLVENTS) IN A HIGH-PRESSURE, HIGH-TEMPERATURE FLOW APPARATUS - LIQUEFACTION OF WOOD AND FURTHER EVIDENCE FOR AN ALTERNATIVE CELLULOSE PULP TECHNOLOGY

Birch wood was treated in a simple flow apparatus with different organic solvents in the supercritical state under Standard conditions. Alcohols showed in the temperature ränge of 250–280°C, at pressures around 100 bar, the highest delignification capability, carbohydrates being attacked too at different rates, while ethers, esters and alkanes preferentially attack the latter. With ethanol the highest ratio of lignin to carbohydrate degradation is achieved, ethanol-water mixtures with 25–50% water content being especially suited for cellulose production. Higher water contents give rise to almost total liquefaction of wood. © 1979, Walter de Gruyter. All rights reserved.; Birkenholz wurde oberhalb der jeweiligen kritischen Temperatur und des kritischen Druckes in einer einfachen Strömungsapparatur mit verschiedenen organischen Lösungsmitteln unter Standardbedingungen behandelt. Alkohole zeigten im Temperaturbereich 250–280°C bei Drücken um 100 bar die höchsten Delignifizierungsraten bei unterschiedlichem Abbau von Kohlenhydraten, während Ether, Ester und Alkane vorwiegend diese angreifen. Ethanol zeigt das günstigste Verhältnis von Lignin- zu Kohlenhydratabbau, wobei Ethanol-Wassergemische mit Wassergehalten von 25–50% sich besonders zur Gewinnung von Cellulose eignen, während bei höheren Wassergehalten das Holz weitgehend verflüssigt werden kann. © 1979, Walter de Gruyter. Alle Rechte vorbehalten.