FATIGUE OF UNIDIRECTIONAL SCS-6/TI-24AL-11NB COMPOSITE CONTAINING A CIRCULAR HOLE

被引：11

作者：

JIRA, JR

LARSEN, JM

机构：

[1] Air Force Materials Directorate, Wright Laboratory, Wright- Patterson Air Force Base, 45433-7817, OH

来源：

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1994年 / 25卷 / 07期

关键词：

D O I：

10.1007/BF02665474

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Fatigue tests of notched unidirectional titanium aluminide composite, SCS-6/Ti-24Al-11Nb (at. pct), were performed to characterize the failure modes and mechanisms that control the life of this material. Using middle-hole specimens tested over a range of stress levels, fatigue damage was documented by optical photography, elastic compliance measurements, and electrical potential drop measurements. It was found that a few dominant cracks form near the notch root and propagate into the composite matrix. Chemical removal of the matrix material and metallographic sectioning of fatigue specimens examined prior to failure revealed that extensive fiber bridging of the matrix cracks dominated the fatigue life. A detailed description of the failure modes and mechanisms of damage initiating in the vicinity of a circular hole is presented, and the relative roles of crack initiation and crack growth are discussed.

引用

页码：1413 / 1424

页数：12

共 21 条

[1]

DAS G, 1993, TITANIUM '92: SCIENCE AND TECHNOLOGY, VOLS 1-3, P2617

[2]

GAMBONE ML, 1990, WRDCTR894145 WRIGHT, V1

[3]

GAMBONE ML, 1990, WRDCTR894145 WRIGHT, V2

[4]

GRESZCZUK LB, ASTM STP, V497, P363

[5]

HARMON DM, 1989, ASTM STP, V1032, P237

[6]

HILLBERRY BM, 1992, J COMPOS TECH RES, V14, P221, DOI 10.1520/CTR10101J

[7]

JIRA JR, 1992, UNPUBLISHED

[8]

JOHN R, 1994, IN PRESS METALL MA A, V25

[9]

JOHNSON HH, 1965, MATER RES STANDARD, V5, P442

[10]

KANTZOS P, 1992, MATER RES SOC SYMP P, V273, P135, DOI 10.1557/PROC-273-135

← 1 2 3 →