EFFECT OF HYDROGEN ON THE MECHANICAL-PROPERTIES OF HIGH-PURITY IRON .1. SOFTENING AND HARDENING OF HIGH-PURITY IRON BY HYDROGEN CHARGING DURING TENSILE DEFORMATION

被引:235
作者
MATSUI, H [1 ]
KIMURA, H [1 ]
MORIYA, S [1 ]
机构
[1] TOHOKU UNIV,GRAD SCH ENGN,SENDAI,MIYAGI 980,JAPAN
来源
MATERIALS SCIENCE AND ENGINEERING | 1979年 / 40卷 / 02期
关键词
D O I
10.1016/0025-5416(79)90191-5
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Tensile tests were performed on high purity iron during hydrogen charging. The flow stress was increased by hydrogen charging below 190 K and was decreased reversibly above 190 K. Hydrogen charging caused no, or only very few, blisters on the surface of specimens with a residual resistivity ratio (RRRH) larger than 3600 but an appreciable number of blisters on less pure specimens (RRRR ≈ 1800). The less pure specimens were hardened rather than softened by hydrogen charging at room temperature. Several mechanisms for the softening are discussed, and it is concluded that the softening and hardening observed in the high purity specimens are the inherent effect of hydrogen on the mechanical properties of iron. The softening and hardening are interpreted as the results of hydrogen-dislocation interactions; it is proposed that hydrogen atoms trapped at the core of a screw dislocation increase its mobility and that hydrogen atoms hinder the motion of edge dislocations at sufficiently low temperatures. © 1979.
引用
收藏
页码:207 / 216
页数:10
相关论文
共 33 条
  • [1] ADAIR AM, 1966, T METALL SOC AIME, V236, P1613
  • [2] LATTICE HARDENING DUE TO DISSOLVED HYDROGEN IN IRON AND STEEL
    ASANO, S
    OTSUKA, R
    [J]. SCRIPTA METALLURGICA, 1976, 10 (11): : 1015 - 1020
  • [3] FURTHER DISCUSSION ON LATTICE HARDENING DUE TO DISSOLVED HYDROGEN IN IRON AND STEEL
    ASANO, S
    OTSUKA, R
    [J]. SCRIPTA METALLURGICA, 1978, 12 (03): : 287 - 288
  • [4] BARANOWSKI B, 1972, BERICH BUNSEN GESELL, V76, P714
  • [5] BEACHEM CD, 1972, METALL TRANS, V3, P437
  • [6] EFFECT OF HYDROGEN ON DEFORMATION OF IRON
    BERNSTEIN, IM
    [J]. SCRIPTA METALLURGICA, 1974, 8 (04): : 343 - 350
  • [7] DILATATION FIELD OF SCREW DISLOCATIONS WITH SPECIAL REFERENCE TO BCC CRYSTALS
    CHOU, YT
    [J]. ACTA METALLURGICA, 1965, 13 (03): : 251 - &
  • [8] FOURNIER R, 1977, 2ND P INT C HYDR MET
  • [9] GIBALA R, 1967, T METALL SOC AIME, V239, P574
  • [10] GONZALEZ OD, 1969, T METALL SOC AIME, V245, P607