MODE OF FORMATION OF SPHERICAL-PARTICLES IN ROLLING CONTACT FATIGUE

被引:42
作者
LOY, B [1 ]
MCCALLUM, R [1 ]
机构
[1] NATL ENGN LAB,GLASGOW,SCOTLAND
关键词
D O I
10.1016/0043-1648(73)90234-2
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
引用
收藏
页码:219 / 228
页数:10
相关论文
共 19 条
[1]  
Barwells FT, 1956, ENGINEERING, V182, P9
[2]   DISCUSSION ON SCANNING ELECTRON MICROSCOPE STUDY OF FRACTURE PHENOMENA ASSOCIATED WITH ROLLING CONTACT SURFACE FATIGUE FAILURE [J].
BROSZEIT, E ;
HESS, FJ .
WEAR, 1971, 17 (04) :314-&
[3]  
BUCHWALD J, 1968, T ASM, V61, P750
[4]  
DAVIES WJ, 1964, P S FATIGUE ROLLING, P23
[5]  
Greenwood J.G., 1957, P C LUBR WEAR I MECH, P314
[6]  
GREENWOOD JA, 1957, P C LUBRICATION WEAR, P800
[7]  
LUND T, 1969, JKA-JERNKONTORET ANN, V153, P337
[8]   MICROSTRUCTURAL ALTERATIONS OF ROLLING - BEARING STEEL UNDERGOING CYCLIC STRESSING [J].
MARTIN, JA ;
BORGESE, SF ;
EBERHARD.AD .
JOURNAL OF BASIC ENGINEERING, 1966, 88 (03) :555-&
[9]   IDENTIFICATION OF POTENTIAL FAILURE NUCLEI IN ROLLING CONTACT FATIGUE [J].
MARTIN, JA ;
EBERHARD.AD .
JOURNAL OF BASIC ENGINEERING, 1967, 89 (04) :932-&
[10]  
MURO M, 1970, WEAR, V15, P309