MELT PROCESSING OF THE Bi2Sr2CaCu2Oy SUPERCONDUCTOR IN OXYGEN AND ARGON ATMOSPHERES

被引：7

作者：

Holesinger, T. G. ^{[1
]}

Miller, D. J. ^{[1
]}

Chumbley, L. S.

机构：

[1] Argonne Natl Lab, Div Mat Sci, 9700 S Cass Ave, Argonne, IL 60439 USA

来源：

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY | 1993年 / 3卷 / 01期

基金：

美国国家科学基金会;

关键词：

D O I：

10.1109/77.233342

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Solidification and subsequent annealing of Bi2Sr2CaCu2Oy (2212) in oxygen and argon atmospheres were investigated in order to identify alternative processing routes for controlling microstructures and superconducting properties. In addition to 2212, several other phases formed on cooling in O-2 and did not disappear upon subsequent annealing. Crystallization in Ar resulted in a divorced eutetic structure of Bi2Sr3-xCaxOy and Cu2O/CuO. The superconductor was formed on subsequent anneals. Samples melted in Ar and then annealed generally possessed a more uniform microstructure compared with samples that were melted in oxygen and annealed. Compositional measurements of the 2212 phase suggest that CaO segregation in the melt may be minimized with an overall composition such as Bi2.15Sr2Ca0.85Cu2Oy

引用

页码：1178 / 1181

页数：4

共 8 条

[1] Bock J., 1990, P ICMC 90 TOP C HIGH
[2] Holesinger T.G., 1992, PHYSICA C UNPUB
[3] CRYSTALLIZATION OF BI-SR-CA-CU-O GLASSES IN OXYGEN
HOLESINGER, TG
MILLER, DJ
CHUMBLEY, LS
[J]. JOURNAL OF MATERIALS RESEARCH, 1992, 7 (07) : 1658 - 1671
[4] SOLID-SOLUTION RANGES OF THE N=2 AND N=3 SUPERCONDUCTING PHASES IN BI2(SRXCA1-X)N+1CUNOY AND THE EFFECT ON TC
HONG, BS
MASON, TO
[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (05) : 1045 - 1052
[5] IMPROVEMENT IN CRITICAL CURRENT-DENSITY OF BI2SR2CA1CU2OX TAPES SYNTHESIZED BY DOCTOR-BLADE CASTING AND MELT GROWTH
KASE, J
IRISAWA, N
MORIMOTO, T
TOGANO, K
KUMAKURA, H
DIETDERICH, DR
MAEDA, H
[J]. APPLIED PHYSICS LETTERS, 1990, 56 (10) : 970 - 972
[6] Miller D.J., 1992, APPL SUPER UNPUB JUL
[7] RAY RD, 1991, PHYSICA C, V172, P435, DOI 10.1016/0921-4534(91)90210-P
[8] Xu Ming, 1991, APPL PHYS LETT, V59, P3640

← 1 →