TENSILE BEHAVIOR OF A NIOBIUM ALUMINA COMPOSITE LAMINATE

被引：13

作者：

BEALS, JT

NARDONE, VC

机构：

[1] United Technologies Research Center, East Hartford, 06108, CT

来源：

JOURNAL OF MATERIALS SCIENCE | 1994年 / 29卷 / 09期

关键词：

D O I：

10.1007/BF00363450

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The tensile properties of a ceramic/metal laminate were examined. Alternating layers of niobium and alumina were fabricated into composite material and tensile tested at room temperature and 982-degrees-C (1800-degrees-F). The tensile behaviour of the laminate material was predicted using established models based on classical laminate theory. The estimated and measured properties showed excellent agreement. Relative to monolithic niobium, the composite material was found to have lower density and substantially higher stiffness.

引用

页码：2526 / 2530

页数：5

共 7 条

[1] THE DEFORMATION AND FRACTURE OF CONSTRAINED METAL SHEETS [J].

BANNISTER, M ;

ASHBY, MF .

ACTA METALLURGICA ET MATERIALIA, 1991, 39 (11) :2575-2582

[2]

BEITSCHER S, 1985, METAL PROGR AUG, P35

[3] DUCTILE REINFORCEMENT TOUGHENING OF GAMMA-TIAL - EFFECTS OF DEBONDING AND DUCTILITY [J].

DEVE, HE ;

EVANS, AG ;

ODETTE, GR ;

MEHRABIAN, R ;

EMILIANI, ML ;

HECHT, RJ .

ACTA METALLURGICA ET MATERIALIA, 1990, 38 (08) :1491-1502

[4] ON THE TOUGHENING OF INTERMETALLICS WITH DUCTILE FIBERS - ROLE OF INTERFACES [J].

DEVE, HE ;

MALONEY, MJ .

ACTA METALLURGICA ET MATERIALIA, 1991, 39 (10) :2275-2284

[5]

HUNT MW, 1992, MATERIALS ENG 1992 M, P222

[6] TOUGHENING OF MOSI2 WITH A DUCTILE (NIOBIUM) REINFORCEMENT [J].

LU, TC ;

EVANS, AG ;

HECHT, RJ ;

MEHRABIAN, R .

ACTA METALLURGICA ET MATERIALIA, 1991, 39 (08) :1853-1862

[7]

PIGGOT MR, 1980, LOAD BEARING FIBRE C, P105

← 1 →