TIN COATINGS ON MILD-STEEL SUBSTRATES WITH ELECTROLESS NICKEL AS AN INTERLAYER

被引:45
作者
CHEN, YI
DUH, JG
机构
[1] Department of Materials Science and Engineering, National Tsing Hua University, Hsinchu
关键词
D O I
10.1016/0257-8972(91)90140-R
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Electroless nickel deposits are incorporated as an interlayer between TiN coatings and mild steel substrates. The electroless nickel layer recrystallizes during r.f. sputtering and a coating assembly of TiN/Ni3/Fe is formed. The employment of electroless nickel results in an increase in the surface hardness as well as the adhesion strength. A Knoop surface hardness as high as 2120 HK5 (close to the hardness of bulk TiN) can be achieved in the interlayer-modified TiN coating.
引用
收藏
页码:163 / 168
页数:6
相关论文
共 12 条
  • [1] AGARWALA RC, 1989, Z METALLKD, V80, P556
  • [2] DEPOSITION OF TIN FILMS WITH TITANIUM INTERLAYER ON LOW-CARBON STEEL BY REACTIVE RF MAGNETRON SPUTTERING
    CHEN, YI
    DUH, JG
    [J]. SURFACE & COATINGS TECHNOLOGY, 1991, 46 (03) : 371 - 384
  • [3] ERMING M, 1988, THIN SOLID FILMS, V166, P273
  • [4] FIELD WD, 1983, METALS HDB, V5, P225
  • [5] Johnson C. E., 1976, Surface Technology, V4, P161, DOI 10.1016/0376-4583(76)90025-X
  • [6] KEYSE RJ, 1987, MATER SCI TECH SER, V3, P963, DOI 10.1179/026708387790220964
  • [7] THE ROLE OF TITANIUM IN THE ABRASIVE WEAR-RESISTANCE OF PHYSICALLY VAPOR-DEPOSITED TIN
    RICKERBY, DS
    BULL, SJ
    ROBERTSON, T
    HENDRY, A
    [J]. SURFACE & COATINGS TECHNOLOGY, 1990, 41 (01) : 63 - 74
  • [8] SPENCER LF, 1974, MET FINISH, P35
  • [9] SPENCER LF, 1975, MET FINISH JAN, P38
  • [10] SPENCER LF, 1974, METAL FINISHING DEC, P58