DUCTILIZATION OF NI3AL BY MACROALLOYING WITH PD

被引：52

作者：

CHIBA, A

HANADA, S

WATANABE, S

机构：

[1] Institute for Materials Research, Tohoku University, Sendai

来源：

ACTA METALLURGICA ET MATERIALIA | 1991年 / 39卷 / 08期

关键词：

D O I：

10.1016/0956-7151(91)90148-T

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Room temperature ductility of Ni3Al was investigated by macroalloying with Pd which is known to have a strong tendency to substitute for the Ni site independent of the composition of the host alloy. A striking feature is that as-cast Pd-doped Ni3Al was successfully rolled by 10-40% reduction without cracking. In addition, elongation to fracture of 11% was obtained in the recrystallized specimen with the composition of Ni75Al23Pd2, whereas not entirely obtained with the composition of Ni73Al25Pd2. It is shown that ductilization of Pd-doped Ni3Al is not explained only by the electronegativity or the valency difference. Instead, it is pointed out that the ductilization of Ll2 ordered intermetallic compounds is associated with ordering energy. The present result on the improvement in ductility of Pd-doped Ni3Al with Al poor composition is consistently interpreted by considering degradation of ordering energy, accompanied with Pd addition and deviation of Al content from stoichiometry.

引用

页码：1799 / 1805

页数：7

共 49 条

[1]

ACKLAND GJ, 1989, MATER RES SOC SYMP P, V133, P105

[2] DUCTILITY OF INTERMETALLIC COMPOUND NI3AL [J].

AOKI, K ;

IZUMI, O .

TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1978, 19 (04) :203-210

[3]

AOKI K, 1977, NIPPON KINZOKU GAKKA, V41, P170

[4] THE EFFECT OF BORON ON THE CHEMISTRY OF GRAIN-BOUNDARIES IN STOICHIOMETRIC NI3AL [J].

BAKER, I ;

SCHULSON, EM ;

MICHAEL, JR .

PHILOSOPHICAL MAGAZINE B-PHYSICS OF CONDENSED MATTER STATISTICAL MECHANICS ELECTRONIC OPTICAL AND MAGNETIC PROPERTIES, 1988, 57 (03) :379-385

[5] INSITU STRAINING OF NI3AL IN A TRANSMISSION ELECTRON-MICROSCOPE [J].

BAKER, I ;

SCHULSON, EM ;

HORTON, JA .

ACTA METALLURGICA, 1987, 35 (07) :1533-1541

[6]

BOND GM, 1987, J MATER RES, V2

[7] THE ORDER-DISORDER TRANSFORMATION IN NI3AL AND NI3AL-FE ALLOYS .2. PHASE-TRANSFORMATIONS AND MICROSTRUCTURES [J].

CAHN, RW ;

SIEMERS, PA ;

HALL, EL .

ACTA METALLURGICA, 1987, 35 (11) :2753-2764

[8] THE ORDER-DISORDER TRANSFORMATION IN NI3AL AND NI3AL-FE ALLOYS .1. DETERMINATION OF THE TRANSITION-TEMPERATURES AND THEIR RELATION TO DUCTILITY [J].

CAHN, RW ;

SIEMERS, PA ;

GEIGER, JE ;

BARDHAN, P .

ACTA METALLURGICA, 1987, 35 (11) :2737-2751

[9] THEORETICAL-STUDIES OF GRAIN-BOUNDARIES IN NI3AL WITH BORON OR SULFUR [J].

CHEN, SP ;

VOTER, AF ;

ALBERS, RC ;

BORING, AM ;

HAY, PJ .

SCRIPTA METALLURGICA, 1989, 23 (02) :217-222

[10] SITE OCCUPATION DETERMINATION OF PD IN NI3AL BY ALCHEMY [J].

CHIBA, A ;

SHINDO, D ;

HANADA, S .

ACTA METALLURGICA ET MATERIALIA, 1991, 39 (01) :13-18

← 1 2 3 4 5 →