INHIBITION OF DEFORMATION TWINNING BY PRECIPITATES IN A MAGNESIUM-ZINC ALLOY

被引:36
作者
CHUN, JS
BYRNE, JG
BORNEMANN, A
机构
[1] Division of Materials Science and Engineering, University of Utah, Salt Lake City, UT
[2] Department of Metallurgy, Stevens Institute of Technology, Hoboken, NJ
关键词
D O I
10.1080/14786436908228701
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Deformation twinning can be inhibited in a Mg-5·1 wt. % Zn alloy by the presence of effective precipitates. This is true even in single crystals favourably oriented for twinning. This resistance to twinning precludes those premature fractures which frequently nucleate at twins. At 4·2°k twinning is highly favoured but effective precipitation postpones it until twice the glide strain observed in quenched crystals with no precipitates. Twin related fracture at 4·2°k is resisted in the fully hardened condition until three times the glide strain for fracture in the quenched condition. In polycrystals, grain size and texture as well as precipitation have profound effects on the deformation mechanism as a function of temperature. The flow stress in the quenched ease can decrease with decreasing temperature when grain size is large and the texture is appropriate for twinning. This behaviour is similar to that of quenched single crystals when twinning predominates. Conversely, the flow stress increases with decreasing temperature when the grain size is small and the texture is inappropriate for twinning. The latter behaviour is characteristic of slip controlled behaviour. Effective precipitation also encourages slip controlled behaviour. A Petch analysis showed very close correlation between the friction stress resisting twin growth in quenched polyerystals and the normal yield stress of single crystals undergoing twinning. © 1969 Taylor & Francis Group, LLC.
引用
收藏
页码:291 / +
页数:1
相关论文
共 24 条
[1]  
ASADA H, 1959, J JAPAN I METALS, V23, P649
[2]   THE DEFORMATION AND FRACTURE OF ALPHA-IRON AT LOW TEMPERATURES [J].
BIGGS, WD ;
PRATT, PL .
ACTA METALLURGICA, 1958, 6 (11) :694-703
[3]   PLASTIC DEFORMATION OF MG-MN ALLOY SINGLE CRYSTALS [J].
BYRNE, JG .
ACTA METALLURGICA, 1963, 11 (09) :1023-&
[4]   A SINGLE-CRYSTAL GROWTH TECHNIQUE FOR ALLOYS WITH WIDE SOLIDIFICATION RANGES [J].
CHUN, JS ;
BYRNE, JG ;
BORNEMAN.A .
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1969, 2 (06) :909-&
[5]  
CHUN JS, TO BE PUBLISHED
[6]   TRANSMISSION ELECTRON MICROSCOPY STUDY OF AGE HARDENING IN A MG-5 WT PER CENT ZN ALLOY [J].
CLARK, JB .
ACTA METALLURGICA, 1965, 13 (12) :1281-&
[7]  
COTTRELL AH, 1958, T AM I MIN MET ENG, V212, P192
[8]  
DELUCA R, 1967, INT C STRENGTH METAL
[9]  
DELUCA R, 1966, THESIS STEVENS I TEC
[10]   TWIN-INDUCED GRAIN BOUNDARY CRACKING IN BCC METALS [J].
GILBERT, A ;
REID, CN ;
HAHN, GT ;
WILCOX, BA .
ACTA METALLURGICA, 1964, 12 (06) :754-&