SYNTHESIS OF GLASS-LIKE CORDIERITE FROM METAL ALKOXIDES AND CHARACTERIZATION BY AL-27 AND SI-29 MASNMR

A sol-gel process for the preparation of glass-like cordiertie and ceramic oxide powder is described. Metal alkoxide precursors were dissolved in 2-methoxyethanol and the metal cations were complexed using 2,4-pentanedione to overcome different hydrolysis rates of metal alkoxides which lead to microscopic inhomogeneities during gelation. Heating the gel in an aerated furnace resulted in ultrafine cordiertie powder of stoichiometric composition at a relatively low temperature. Cordierite gel and glass were also prepared by other methods and compared with the above gel. The environments of aluminum and silicon in the glass and gels heated at various temperatures were studied using Al-27 and Si-29 magic angle spinning nuclear magnetic resonance (MAS-NMR) spectroscopy. Most of the heated gels and the glass showed resonances due to pentacoordinated aluminum along with 4- and 6-coordinated aluminum. The homogeneities of the resulting gels and glass are compared using the MASNMR data.