CHARACTERISTIC LENGTH OF GLASS-TRANSITION - EXPERIMENTAL-EVIDENCE

被引:127
作者
SCHICK, C [1 ]
DONTH, E [1 ]
机构
[1] TH CARL SCHORLEMMER LEUNA MERSEBURG,O-4200 MERSEBURG,GERMANY
来源
PHYSICA SCRIPTA | 1991年 / 43卷 / 04期
关键词
D O I
10.1088/0031-8949/43/4/010
中图分类号
O4 [物理学];
学科分类号
0702 ;
摘要
The glass transition length scale determined from formulae of a fluctuation approach (2-zeta-a = 2...5 nm) is confirmed by two independent experimental methods. Firstly the glass transition parameters in self-organized amorphous layers of variable thickness in semicrystalline poly(ethylene terephtalate) show significant sensitivity to the nanometer length scale of zeta-a. The results can be explained by a direct influence of spatial limitations on the large mode lengths of the glass transition. Secondly, the analysis of the arrangement of different system responses across the glass transition zone at constant temperature in polystyrene and poly(vinyl acetate) results in the location of zeta-a between the limits 0.6 nm (from local modes) and 10 nm (entanglement spacing). Experimental temperature dependencies of spectral widths are discussed with those obtained from the fluctuation approach. The report also contains a discussion of the presumed general scaling principle: At a given state, short mode length corresponds to high frequency (mobility) and vice versa.
引用
收藏
页码:423 / 429
页数:7
相关论文
共 57 条
[1]   LONGITUDINAL VISCOELASTIC RELAXATION IN AMORPHOUS POLYBUTADIENE BY DYNAMIC LIGHT-SCATTERING AND ULTRASONIC-ABSORPTION [J].
ALIG, I ;
STIEBER, F ;
WARTEWIG, S ;
FYTAS, G .
POLYMER, 1988, 29 (06) :975-980
[2]   GLASS-TRANSITION TEMPERATURES FOR SIMPLE MOLECULAR LIQUIDS AND THEIR BINARY-SOLUTIONS [J].
ANGELL, CA ;
SARE, JM ;
SARE, EJ .
JOURNAL OF PHYSICAL CHEMISTRY, 1978, 82 (24) :2622-2629
[3]   SPECIFIC-HEAT SPECTROSCOPY OF THE GLASS-TRANSITION [J].
BIRGE, NO ;
NAGEL, SR .
PHYSICAL REVIEW LETTERS, 1985, 54 (25) :2674-2677
[4]   BRILLOUIN-SCATTERING STUDIES OF STRUCTURAL RELAXATIONS IN POLY(PROPYLENE GLYCOL) [J].
BORJESSON, L ;
STEVENS, JR ;
TORELL, LM .
POLYMER, 1987, 28 (11) :1803-1808
[5]   GLASS-TRANSITION AND MELTING BEHAVIOR OF POLY(THIO-1,4-PHENYLENE) [J].
CHENG, SZD ;
WU, ZQ ;
WUNDERLICH, B .
MACROMOLECULES, 1987, 20 (11) :2802-2810
[6]   FREQUENCY-DEPENDENT SPECIFIC-HEAT AND THERMAL-CONDUCTIVITY AT THE GLASS-TRANSITION IN ORTHO-TERPHENYL MIXTURES [J].
DIXON, PK ;
NAGEL, SR .
PHYSICAL REVIEW LETTERS, 1988, 61 (03) :341-344
[8]   FINE-STRUCTURE OF THE GLASS-TRANSITION IN AMORPHOUS POLYMERS .2. INTERPRETATION OF THE G''-PEAK AND J''-PEAK BY DIFFERENT MOLECULAR-MOTION [J].
DONTH, E ;
SCHNEIDER, K .
ACTA POLYMERICA, 1985, 36 (05) :273-278
[9]   FINE-STRUCTURE OF THE GLASS-TRANSITION IN AMORPHOUS POLYMERS .1. INTERPRETATION OF SHEAR CURVES WITH THE AID OF THE FLUCTUATION DISSIPATION THEOREM [J].
DONTH, E ;
SCHNEIDER, K .
ACTA POLYMERICA, 1985, 36 (04) :213-215
[10]  
DONTH E, 1981, GLASUBERGANG