CHARACTERIZATION OF METALLURGICAL GRADE SILICON

Optical metallography, scanning electron microscopy, electron microprobe analysis, and transmission electron microscopy were used to characterize metallurgical grade silicon, produced in an electric arc furnace. Coincidence fraction determinations were assumed to be Σ7 and Σ9 when grain boundaries are underlined by precipitated phases and Σ3 when they are not. The study of intergranular compounds was emphasized; ten compounds were found, the main ones being Si2Ca, Si8Al6Fe4Ca, Si2Al2Ca, Si2FeTi, and Si2.4Fe (α leboite). The precipitation of these compounds was discussed according to the principal impurity concentrations in silicon. The crystalline structure of Si8Al6Fe4Ca was determined to be triclinic with a = 1.3923 nm, b = 1.3896 nm, c = 1.3900 nm and α = 92.4°, β = 110.3°, γ = 119.9°. © 1990, Materials Research Society. All rights reserved.