EFFECT OF ELECTRODEPOSITION PARAMETERS ON THE MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF CO-NI ALLOYS

被引：33

作者：

FENINECHE, N ^{[1
]}

CODDET, C ^{[1
]}

SAIDA, A ^{[1
]}

机构：

[1] BULL PERIPHERIQUES,BELFORT,FRANCE

来源：

SURFACE & COATINGS TECHNOLOGY | 1990年 / 41卷 / 01期

关键词：

D O I：

10.1016/0257-8972(90)90131-U

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The effect of chloride bath plating conditions on the microstructure of Co-Ni deposits and related properties such as hardness, brittleness and tensile strength was studied. Bright smooth deposits with a high current efficiency (93%) were obtained at room temperature with current densities of 1.0-1.5 A dm-2 at pH 3.5. Hard greyish deposits of Co-Ni alloys with pits in the middle and some peeling at the edges were obtained when the current density was 3.0 A dm-2 at pH 3.5 and at room temperature. X-ray analysis confirmed that the deposited Co-Ni alloy was a solid solution with an h.c.p. lattice. © 1990.

引用

页码：75 / 81

页数：7

共 17 条

[1] ELECTROCRYSTALLIZATION OF ZINC ON COPPER SINGLE-CRYSTAL PLANES UNDER INFLUENCE OF AN ASYMMETRIC ALTERNATING-CURRENT [J].