BORON-NITRIDE INTERPHASE IN CERAMIC-MATRIX COMPOSITES

被引:184
作者
NASLAIN, R
DUGNE, O
GUETTE, A
SEVELY, J
BROSSE, CR
ROCHER, JP
COTTERET, J
机构
[1] CEMES,OPT ELECTR LAB,CNRS,F-31055 TOULOUSE,FRANCE
[2] SOC EUROPEAN PROPULS,F-33165 ST MEDARD,FRANCE
关键词
D O I
10.1111/j.1151-2916.1991.tb06789.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A BN interphase has been deposited, by isothermal/isobaric chemical vapor infiltration (ICVI) from BF3-NH3, within a preform made from ex-polycarbosilane (ex-PCS) fibers, at about 1000-degrees-C. In a second step, the BN-treated preform was densified with SiC deposited from CH3SiCl3-H2 at about the same temperature. From a thermodynamic standpoint, ex-PCS fibers could be regarded as unreactive vs the BF3-NH3 gas phase assuming they are coated with a thin layer of carbon or/and silica. The as-deposited interphase consists of turbostratic BN (N/B < 1) containing oxygen. The SiC infiltration acts as annealing treatment: (i) the BN inter-phase becomes almost stoichiometric and free of oxygen; (ii) the fibers undergo a decomposition process yielding a SiO2/C layer at the BN/fiber interface. The weaker link in the interfacial sequence seems to be the BN/SiO2 interface. Deflection of microcracks arising from the failure of the matrix takes place at (or nearby) that particular interface.
引用
收藏
页码:2482 / 2488
页数:7
相关论文
共 31 条
[1]  
BENDER B, 1986, AM CERAM SOC BULL, V65, P363
[2]  
BRENNAN JJ, 1986, TAILORING MULTIPHASE, V20, P549
[3]  
CHAIM R, 1987, ADV CERAM MATER, V2, P154
[4]  
CHRISTIN F, 1979, 7TH P INT C CVD LOS, P499
[5]  
DUGNE O, UNPUB J MATER SCI
[6]  
DUGNE O, 1989, MAR P ECCM BORD, V3, P129
[7]  
DUGNE O, 1989, THESIS U BORDEAUX BO
[8]  
DUGNE O, UNPUB THIN SOLID FIL
[9]  
DUGNE O, UNPUB J LESS COMMON
[10]  
ERIKSSON G, 1975, CHEM SCRIPTA, V8, P100