APPLICATION OF THE PARIS EQUATION TO THE FATIGUE GROWTH OF TRANSVERSE PLY CRACKS

被引:70
作者
BONIFACE, L
OGIN, SL
机构
关键词
D O I
10.1177/002199838902300706
中图分类号
TB33 [复合材料];
学科分类号
摘要
引用
收藏
页码:735 / 754
页数:20
相关论文
共 41 条
[1]   A 3-D FRACTURE-MECHANICS APPROACH TO THE STRENGTH OF COMPOSITE-MATERIALS [J].
ALTUS, E ;
ROTEM, A .
ENGINEERING FRACTURE MECHANICS, 1981, 14 (03) :637-&
[2]  
BADER MG, 1985, 5TH P INT C COMP MAT, P221
[3]  
BAILEY JE, 1981, J MATER SCI, V16, P649, DOI 10.1007/BF02402782
[4]   TRANSVERSE CRACKING AND LONGITUDINAL SPLITTING BEHAVIOR OF GLASS AND CARBON-FIBER REINFORCED EPOXY CROSS PLY LAMINATES AND THE EFFECT OF POISSON AND THERMALLY GENERATED STRAIN [J].
BAILEY, JE ;
CURTIS, PT ;
PARVIZI, A .
PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES, 1979, 366 (1727) :599-&
[5]  
BONIFACE L, 1985, 1ST P EUR C COMP MAT, P57
[6]  
BROUTMAN LJ, 1969, 24TH P ANN TECH C NE, P1
[7]   ANALYSIS OF PROGRESSIVE MATRIX CRACKING IN COMPOSITE LAMINATES .2. 1ST PLY FAILURE [J].
DVORAK, GJ ;
LAWS, N .
JOURNAL OF COMPOSITE MATERIALS, 1987, 21 (04) :309-329
[8]   ANALYSIS OF PROGRESSIVE MATRIX CRACKING IN COMPOSITE LAMINATES .1. THERMOELASTIC PROPERTIES OF A PLY WITH CRACKS [J].
DVORAK, GJ ;
LAWS, N ;
HEJAZI, M .
JOURNAL OF COMPOSITE MATERIALS, 1985, 19 (03) :216-234
[9]   EXPERIMENTAL-DETERMINATION OF THE INSITU TRANSVERSE LAMINA STRENGTH IN GRAPHITE EPOXY LAMINATES [J].
FLAGGS, DL ;
KURAL, MH .
JOURNAL OF COMPOSITE MATERIALS, 1982, 16 (MAR) :103-116
[10]   PREDICTION OF TENSILE MATRIX FAILURE IN COMPOSITE LAMINATES [J].
FLAGGS, DL .
JOURNAL OF COMPOSITE MATERIALS, 1985, 19 (01) :29-50