ARGON SORPTION AND PARTIAL MOLAR VOLUME IN POLY(ETHYL METHACRYLATE) ABOVE AND BELOW THE GLASS-TRANSITION TEMPERATURE

被引:26
作者
KAMIYA, Y
MIZOGUCHI, K
NAITO, Y
BOURBON, D
机构
[1] Industrial Products Research Institute, Tsukuba, Ibaraki, 305
关键词
D O I
10.1002/polb.1991.090290208
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Sorption and dilation isotherms for argon in poly(ethyl methacrylate) (PEMA) are reported for pressures up to 50 atm over the temperature range 5-85-degrees-C. At temperatures below the glass transition (T(g) = 61-degrees-C), sorption isotherms are well described by the dual-mode sorption model; and isotherms above T(g) follow Henry's law. However, isotherms for dilation due to sorption are linear in pressure at all temperatures over the range investigated. Partial molar volumes of Ar in PEMA are obtained from these isotherms. The volumes are approximately constant above T(g) (about 40 cm3/mol), whereas the volumes below T(g) are smaller and dependent on both temperature and concentration (19-26 cm3/mol). By analyzing the experimental data according to the dual-mode sorption and dilation model, the volume occupied by a dissolved Ar molecule and the mean size of microvoid in the glass are estimated to be 67 and 129 angstrom 3, respectively. The cohesive energy density of the polymer is also estimated as 61 cal/cm3 from the temperature dependence of the dual-mode parameters.
引用
收藏
页码:225 / 234
页数:10
相关论文
共 25 条
[1]   SORPTION AND DIFFUSION IN ETHYL CELLULOSE .3. COMPARISON BETWEEN ETHYL CELLULOSE AND RUBBER [J].
BARRER, RM ;
BARRIE, JA ;
SLATER, J .
JOURNAL OF POLYMER SCIENCE, 1958, 27 (115) :177-197
[2]   EFFECT OF SUB-TG ANNEALING ON CO2 SORPTION IN POLYCARBONATE [J].
CHAN, AH ;
PAUL, DR .
POLYMER ENGINEERING AND SCIENCE, 1980, 20 (01) :87-94
[3]   GAS SORPTION AND PERMEATION IN POLY(ETHYL METHACRYLATE) [J].
CHIOU, JS ;
PAUL, DR .
JOURNAL OF MEMBRANE SCIENCE, 1989, 45 (1-2) :167-189
[4]   GAS AND VAPOR SORPTION IN POLYMERS JUST BELOW TG [J].
CHIOU, JS ;
MAEDA, Y ;
PAUL, DR .
JOURNAL OF APPLIED POLYMER SCIENCE, 1985, 30 (10) :4019-4029
[5]   DILATION OF POLYMERS BY SORPTION OF CARBON-DIOXIDE AT ELEVATED PRESSURES .1. SILICONE-RUBBER AND UNCONDITIONED POLYCARBONATE [J].
FLEMING, GK ;
KOROS, WJ .
MACROMOLECULES, 1986, 19 (08) :2285-2291
[6]  
Gee G., 1966, POLYMER, V7, P177
[7]   DIE ISOTHERME KOMPRESSIBILITAT EINIGER AMORPHER UND TEILKRISTALLINER HOCHPOLYMERER IM TEMPERATURBEREICH VON 20-250 DEGREES C UND BEI DRUCKEN BIS ZU 2000 KP/CM2 [J].
HELLWEGE, KH ;
KNAPPE, W ;
LEHMANN, P .
KOLLOID-ZEITSCHRIFT AND ZEITSCHRIFT FUR POLYMERE, 1962, 183 (02) :110-&
[8]   DILATION OF POLYETHYLENE BY SORPTION OF CARBON-DIOXIDE [J].
HIROSE, T ;
MIZOGUCHI, K ;
KAMIYA, Y .
JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 1986, 24 (09) :2107-2115
[9]   SOLUBILITY, ENTROPY AND PARTIAL MOLAL VOLUMES IN SOLUTIONS OF GASES IN NON-POLAR SOLVENTS [J].
JOLLEY, JE ;
HILDEBRAND, JH .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1958, 80 (05) :1050-1054
[10]   GRAVIMETRIC STUDY OF HIGH-PRESSURE SORPTION OF GASES IN POLYMERS [J].
KAMIYA, Y ;
HIROSE, T ;
MIZOGUCHI, K ;
NAITO, Y .
JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 1986, 24 (07) :1525-1539