MAGNETIC-PROPERTIES OF FECU (3D TRANSITION-METALS) SIB ALLOYS WITH FINE-GRAIN STRUCTURE

被引:31
作者
SAWA, T [1 ]
TAKAHASHI, Y [1 ]
机构
[1] TOSHIBA CO LTD,DIV MET PROD,YOKOHAMA 235,JAPAN
关键词
D O I
10.1063/1.345886
中图分类号
O59 [应用物理学];
学科分类号
摘要
Soft magnetic properties were investigated together with crystallization process and grain size for FeCu (3d transition metals) SiB alloys with fine grains. They were rapidly quenched from the melt to achieve amorphous states and then annealed above their crystallization temperatures. In the group of 3d transition metals studied, low magnetic core loss at high frequency was obtained for V-substituted Fe-based alloys, because only a bcc Fe solid solution with diameter of about 20 nm precipitated. On the other hand, Cr- or Mn-substituted alloys could not be attained with good soft magnetic properties because of the existence of Fe-metalloid compounds besides the bcc phase by annealing above their crystallization temperatures. The effect of grain size on the soft magnetic properties is more prominent at lower frequency. Diffraction peaks which are characteristics of an ordered phase (DO3) are observed, which is the origin of excellent soft magnetic properties in FeAlSi alloys.
引用
收藏
页码:5565 / 5567
页数:3
相关论文
共 5 条
  • [1] HERZER G, 1989, INTERMAG 89 WASH
  • [2] MAGNETOSTRICTION AND MAGNETIC CORE LOSS AT HIGH-FREQUENCY IN AMORPHOUS FE-NB-SI-B ALLOYS
    INOMATA, K
    HASEGAWA, M
    KOBAYASHI, T
    SAWA, T
    [J]. JOURNAL OF APPLIED PHYSICS, 1983, 54 (11) : 6553 - 6557
  • [3] Luborsky F. E., 1983, Amorphous metallic alloys, P360
  • [4] Takahashi M., 1987, Proceedings of the International Symposium on Physics of Magnetic Materials, P414
  • [5] YOSHIZAWA Y, 1988, J APPL PHYS, V64, P6054