RUBBER TOUGHENING OF POLYSTYRENE THROUGH REACTIVE BLENDING

Acrylonitrile-butadiene rubber having carboxylic acid groups (XNBR) and polystyrene having oxazoline groups, were melt blended in a Rheomix mixer under optimized conditions. The ratio of rubber to polystyrene phase was kept constant at 1:4 by weight. The concentration of the reactive oxazoline groups in the polystyrene phase was varied by mixing polystyrene (PS) with a copolymer of styrene and vinyl oxazoline (OPS). A torque rise observed during blending was found to be related to the concentration of oxazoline-carboxylic acid pairs. This torque rise, and independently measured increases in viscosity, both indicate inter-polymer crosslinking. Scanning electron microscopy was used to observe the morphology of the blends. Improved rubber phase dispersion was observed with increasing oxazoline concentration. Instrumented impact strength measurements were made using an unnotched Charpy technique.