DRY SLIDING WEAR BEHAVIOR OF SQUEEZE CAST-ALUMINUM ALLOY SILICON-CARBIDE COMPOSITES

被引:152
作者
MODI, OP [1 ]
PRASAD, BK [1 ]
YEGNESWARAN, AH [1 ]
VAIDYA, ML [1 ]
机构
[1] INDIAN INST TECHNOL,DEPT MET ENGN,KANPUR 208016,UTTAR PRADESH,INDIA
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1992年 / 151卷 / 02期
关键词
D O I
10.1016/0921-5093(92)90212-J
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Squeeze cast Al alloy (BSS:LM11) matrix composites, each containing 10 vol.% of SiC particles or fibres, have been investigated for their resistance to dry wear under varying applied pressures (1-3 MPa) at a sliding speed of 2.68 m s-1 against a rotating EN25 steel disc. Seizure pressure of the composites as well as the base alloy was determined using a pin-on-disc machine. The alloy containing SiC particles showed less wear rate than the one having SiC fibre dispersion. The base alloy showed maximum rate of wear. Dispersoid-matrix interfacial bonding and shape of the dispersoid were found to play an important role in governing the wear rate of the composites. Scanning electron microscopy examinations indicated relatively finer grooves on the wear surfaces prior to seizure, while seizure led to severely damaged surfaces. Similarly, wear debris generated during wear was thin and flaky prior to seizure, while bulky debris particles were observed during seizure. A few iron machining chips were also found in all the cases. The results obtained have been explained on the basis of wear-induced microstructural changes and deformation, leading to work hardening in the subsurface regions and wear debris.
引用
收藏
页码:235 / 245
页数:11
相关论文
共 23 条
[1]   SLIDING AND ABRASIVE WEAR BEHAVIOR OF AN ALUMINUM (2014)-SIC PARTICLE REINFORCED COMPOSITE [J].
ALPAS, AT ;
EMBURY, JD .
SCRIPTA METALLURGICA ET MATERIALIA, 1990, 24 (05) :931-935
[2]  
ASHBY MF, COMMUNICATION
[3]  
BHANSALI KJ, 1982, J MET, V32, P30
[4]  
DAS AA, 1988, CAST METALS, V1, P69
[5]   TRIBOLOGY OF AL-SI ALLOY-GRAPHITE COMPOSITES - TRIBOINDUCED GRAPHITE FILMS AND THE ROLE OF SILICON MORPHOLOGY [J].
DAS, S ;
PRASAD, SV ;
RAMACHANDRAN, TR .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 138 (01) :123-132
[6]   THEORETICAL-ANALYSIS OF DRY FRICTION IN BRITTLE AND DUCTILE MATERIALS [J].
DECELIS, B .
WEAR, 1987, 116 (03) :287-298
[7]  
GLAESER WA, 1983, APR P INT C TRIB 80S, V1, P219
[8]   COMPOSITES OF ALUMINUM-ALLOYS - FABRICATION AND WEAR BEHAVIOR [J].
HOSKING, FM ;
PORTILLO, FF ;
WUNDERLIN, R ;
MEHRABIAN, R .
JOURNAL OF MATERIALS SCIENCE, 1982, 17 (02) :477-498
[9]  
Jolly M. R., 1990, FOUNDRYMAN, V83, P509
[10]   Wear-mechanism maps [J].
Lim, S. C. ;
Ashby, M. F. .
ACTA METALLURGICA, 1987, 35 (01) :1-24