THE INFLUENCE OF THE SI AND MN CONCENTRATIONS ON THE KINETICS OF THE BAINITE TRANSFORMATION IN FE-C-SI-MN ALLOYS

Five Fe-C-Si-Mn alloys were investigated by dilatometry, optical microscopy, and transmission electron microscopy (TEM) analysis to determine the effects of Si and Mn content and austenitizing temperatures on the kinetics of bainite transformation. Segregation of Mn at prior austenite grain boundaries at a temperature below Bs was detected by the scanning transmission electron microscopy + energy dispersive spectroscopy (STEM + EDS) and secondary ion mass spectroscopy (SIMS) techniques. The fraction of intragranular ferrite increases with Mn content. The time needed for the initiation of the bainite transformation tends to decrease as the austenitizing temperature decreases. The results obtained were compared with those from Fe-0.38C-1.73Si and Fe-0.38C-3.11Mn alloys. Equilibrium and nonequilibrium segregation of Mn at prior austenite grain boundaries and the effect of the interaction between Si and Mn on the segregation of Mn are used to explain the results obtained and the large difference between the kinetics of the two ternary alloys and those of the Fe-C-Si-Mn alloys. © 1990 The Metallurgical of Society of AIME.