CRACK GROWTH AND PREDICTION OF ENDURANCE IN THERMAL-MECHANICAL FATIGUE OF 12CR-MO-V-W STEEL

被引：9

作者：

KOIZUMI, T

OKAZAKI, M

机构：

[1] Faculty of Engineering, Tokyo Institute of Technology, Tokyo, Meguro-ku

[2] Tokyo Institute of Technology, Tokyo, Meguro-ku

来源：

FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES | 1979年 / 1卷 / 04期

关键词：

D O I：

10.1111/j.1460-2695.1979.tb01337.x

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Abstract Fractography and fracture mechanics were used to study the behaviour of a crack that emanated from a starter notch on a specimen surface subjected to thermal cycles, and which grew in the direction perpendicular to the surface, under out‐of‐phase loading conditions. A 12Cr–Mo–V–W steel was used as representative of an elevated temperature material, and one that is frequently employed for vessels or heat‐exchanger tubes. A low power travelling microscope observed crack length changes on the specimen surface. It was shown that the growth rate of a part‐through crack could be expressed in terms of a strain intensity factor range and two constants, and that the striation spacings agreed with the microscopically observed crack growth rate. The integration of the crack growth rate equation gave an approximate evaluation of thermal fatigue life of smooth specimens. Copyright © 1979, Wiley Blackwell. All rights reserved

引用

页码：509 / &

共 9 条

[1]

Wareing J., Vaughan H.G., The relationship between striation spacing, macroscopic crack growth rate and the low‐cycle fatigue life of a Type 316 stainless steel at 625°C, Metal Sci., 11, pp. 439-446, (1977)

[2]

Yamaguchi K., Kanazawa K., Yoshida S., Dependence of temperature and strain rate on the low‐cycle fatigue life of type 321 stainless steel (in Japanese), J. Iron Steel Inst. of Japan, 64, pp. 1199-1208, (1978)

[3]

Koizumi T., Okazaki M., Shibuya T., Thermal fatigue crack propagation in cast steel, J. Japan Soc. Mater. Sci., 28, pp. 428-434, (1979)

[4]

Smith F.W., Stress intensity factors for a semi‐elliptical surface flow, pp. 1-29, (1966)

[5]

Boettner R.C., Laird C., McEvilly A.J., Crack nucleation and growth in high strain‐low cycle fatigue, Trans. Metall. Soc. AIME, 233, pp. 379-387, (1965)

[6]

Rau C.A., Gemma A.E., Leverant G.R., pp. 166-178, (1973)

[7]

Hirano K., Koizumi T., Nakazawa H., A fracture mechanics and fractographic study on thermal fatigue of cast irons (in Japanese), Transactions of the Japan Society of Mechanical Engineers, 42, pp. 2673-2678, (1976)

[8]

Laird C., pp. 131-168, (1967)

[9]

Taira S., Ohnami M., A contribution to standardization of testing method for thermal fatigue (in Japanese), J. Japan Soc. Mater. Sci., 23, pp. 219-223, (1974)

← 1 →