SLOW FATIGUE CRACK GROWTH AND THRESHOLD BEHAVIOR IN AIR AND VACUUM OF COMMERCIAL ALUMINUM-ALLOYS

被引：93

作者：

KIRBY, BR

BEEVERS, CJ

机构：

[1] Department of Physical Metallurgy and Materials Science, University of Birmingham, Birmingham, B15 2TT, Edgbaston

来源：

FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES | 1979年 / 1卷 / 02期

关键词：

D O I：

10.1111/j.1460-2695.1979.tb00378.x

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Abstract— Fatigue crack growth and threshold behaviour have been examined in three commercial aluminium alloys in both air and vacuum environments. It was observed that, in air, the threshold stress intensity range ΔKt, varied linearly with the ΔKt ratio. In contrast ΔK, in vacuum was found to be independent of R. Over the whole growth rate range examined fatigue crack growth in vacuum was ΔK controlled and failure occurred by a dimple and ductile striation mechanism. This also applied to failure in the intermediate growth rate ranges in air. However, at slow growth rates in air, fatigue crack growth was structure sensitive and crystallographic facets were formed during the crack propagation process. Copyright © 1979, Wiley Blackwell. All rights reserved

引用

页码：203 / &

共 39 条

[1] Paris P.C., Erdogan F., A critical analysis of crack propagation laws, Journal of Basic Engineering, 85, (1963)
[2] Schmidt R.A., Paris P.C., Threshold for fatigue crack propagation and the effects of load ratio and frequency, A.S.T.M. STP, 536, (1973)
[3] Paris P.C, Bucci R.J., Wessel E.T., Anderson A.F., On the threshold for fatigue crack growth, (1971)
[4] Cooke R.J., Beevers C.J., The effect of load ratio on the threshold stresses for fatigue crack propagation in medium carbon steels, Engng Fracture Mech., 5, (1973)
[5] Cooke R.J., Beevers C.J., Slow fatigue crack propagation in pearlitic steels, Mater. Sci. Engng, 13, (1974)
[6] Cooke R.J., Irving P.E., Booth G.S., Beevers C.J., The slow fatigue crack growth and threshold behaviour of a medium‐carbon alloy steel in air and vacuum, Engng Fracture Mech., 7, (1975)
[7] Klesnil M., Lukas P., Effect of stress cycle asymmetry on fatigue crack growth, Mater. Sci. Engng, 9, (1972)
[8] Klesnil M., Lukas P., The influence of strength and stress history on growth and stabilisation of fatigue cracks, Engng Fracture Mech., 4, (1972)
[9] Irving P.E., Beevers C.J., Microstructural influences on fatigue crack growth in Ti–6A1–4V, Mater. Sci. Engng, 14, (1979)
[10] Pook L., (1972)

← 1 2 3 4 →