INTERNAL FRICTION IN COPPER AND ALPHA-BRASSES DURING PLASTIC DEFORMATION

The internal friction Q-1 of annealed copper and α-brass wires containing 10, 20, 30 and 35 at. % of zinc was studied by a torsional oscillation method during plastic deformation. The results are interpreted in terms of two theoretical models ascribing the amplitude-dependent internal friction, observed in the pre-yield stage, to coupling of the cyclic stress with the creep component of the deformation, and the amplitude-independent internal friction at larger, plastic, strains to losses arising from contributions of the torsional stress to the plastic deformation. Up to the maximum tensile strain of 1 % used in the experiments, the influence of zinc content on Q-1 is not pronounced. © 1969 Chapman and Hall.