HYDROGEN STORAGE PROPERTIES OF THE MMNI4.6SN0.4 SYSTEM

被引:19
作者
MUNGOLE, MN [1 ]
BALASUBRAMANIAM, R [1 ]
RAI, KN [1 ]
SINGH, KP [1 ]
机构
[1] INDIAN INST TECHNOL,BIOL & MED RES PROGRAM,KANPUR 208016,UTTAR PRADESH,INDIA
关键词
D O I
10.1016/0360-3199(92)90073-6
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The hydrogen absorption and desorption characteristics of cast and annealed MmNi4.6Sn0.4 intermetallic have been investigated in the temperature range 278-308 K. Hydride formation pressure is in the range of 4-10 atm in the above temperature range. The ease of hydriding of MmNi4.6Sn0.4 has been related to an increase in the unit cell volume of MmNi5 with Sn substitution. The enthalpies of hydride formation for the as-cast and annealed conditions are -26.33 kJ mol-1 H-2 and -25.53 kJ mol-1 H-2, respectively. The entropies of hydride formation are -108.21 J K-1 mol-1 H-2 and -105.49 J K-1 mol-1 H-2 for the as-cast and annealed intermetallic, respectively. Annealing markedly flattened the plateau pressure and increased the hysteresis at any fixed temperature. Hysteresis reduced with increasing temperature for both the cast and annealed conditions. The hydrogen storage capacity (i.e. the maximum H/M) was limited to 0.6.
引用
收藏
页码:603 / 606
页数:4
相关论文
共 18 条
  • [1] BUSCH G, 1977, AUG P INT S HYDR EN, P293
  • [2] THE EFFECT OF ANNEALING ON PLATEAU HYDROGEN PRESSURES AND HYSTERESIS IN THE LANI5-H SYSTEM
    FLANAGAN, TB
    BIEHL, GE
    [J]. JOURNAL OF THE LESS-COMMON METALS, 1981, 82 (1-2): : 385 - 389
  • [3] SORPTION HYSTERESIS IN LANI5-H AND SMCO5-H SYSTEMS
    KUIJPERS, FA
    VANMAL, HH
    [J]. JOURNAL OF THE LESS-COMMON METALS, 1971, 23 (04): : 395 - &
  • [4] CORRELATION BETWEEN INTERSTITIAL HOLE SIZES IN INTERMETALLIC COMPOUNDS AND THERMODYNAMIC PROPERTIES OF HYDRIDES FORMED FROM THOSE COMPOUNDS
    LUNDIN, CE
    LYNCH, FE
    MAGEE, CB
    [J]. JOURNAL OF THE LESS-COMMON METALS, 1977, 56 (01): : 19 - 37
  • [5] LUNDIN CE, 1977, DEC P INT C ALT EN S, P3803
  • [6] LUNDIN CE, 1980, SCRIPTA METALL, V14, P443
  • [7] HYDROGEN STORAGE OF MMNI5-XALX SYSTEM BASED ON INDIAN MISCHMETAL
    MUNGOLE, MN
    RAI, KN
    SINGH, KP
    [J]. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1991, 16 (08) : 545 - 549
  • [8] HYDROGEN STORAGE PROPERTIES OF MMNI5-XMNX SYSTEM BASED ON INDIAN MISCHMETAL
    MUNGOLE, MN
    RAI, KN
    BALASUBRAMANIAM, R
    SINGH, KP
    [J]. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 1992, 17 (08) : 607 - 611
  • [9] ABSORPTION-DESORPTION CHARACTERISTICS OF HYDROGEN FOR MISCHMETAL-NICKEL-COBALT ALLOYS
    OSUMI, Y
    SUZUKI, H
    KATO, A
    NAKANE, M
    MIYAKE, Y
    [J]. NIPPON KAGAKU KAISHI, 1979, (06) : 722 - 726
  • [10] ABSORPTION-DESORPTION CHARACTERISTICS OF HYDROGEN FOR MISCHMETAL-NICKEL-MANGANESE ALLOYS
    OSUMI, Y
    SUZUKI, H
    KATO, A
    NAKANE, M
    MIYAKE, Y
    [J]. NIPPON KAGAKU KAISHI, 1979, (01) : 45 - 48